Corrosion resistance of PM2000 ODS steel in high temperature supercritical carbon dioxide

被引：24

作者：

Firouzdor, V. ^{[1
]}

Cao, G. P. ^{[1
]}

Sridharan, K. ^{[1
]}

Anderson, M. ^{[1
]}

Allen, T. R. ^{[1
]}

机构：

[1] Univ Wisconsin, Dept Engn Phys, Madison, WI 53706 USA

来源：

MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION | 2015年 / 66卷 / 02期

关键词：

ALLOYS;

D O I：

10.1002/maco.201307223

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Corrosion of PM2000 ODS steel in supercritical CO2 at 650 degrees C and 20 MPa for 3000 h was studied. The corrosion performance of the alloys was evaluated by weight change measurements, and the surface oxide scale was characterized by scanning electron microscopy, X-ray diffraction, and X-ray photoelectron spectroscopy. PM2000 ODS steel showed significantly better corrosion resistance compared to austenitic stainless steels and nickel based alloys tested in the same conditions. The high corrosion resistance is attributed to the formation of a dense and protective aluminum-rich oxide layer on the surface. The oxide layer thickness was only about 200 nm after 3000 h exposure.

引用

页码：137 / 142

页数：6

共 25 条

[11] THERMAL-STABILITY OF DISPERSOIDS IN FERRITIC OXIDE DISPERSION-STRENGTHENED ALLOYS [J].

KRAUTWASSER, P ;

CZYRSKAFILEMONOWICZ, A ;

WIDERA, M ;

CARSUGHI, F .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1994, 177 (1-2) :199-208

[12]

Lim J. Y., 2010, THESIS MIT

[13]

Lim J. Y., 2008, P NACE 2008 NEW ORL, P17

[14] Recent developments in irradiation-resistant steels [J].

Odette, G. R. ;

Alinger, M. J. ;

Wirth, B. D. .

ANNUAL REVIEW OF MATERIALS RESEARCH, 2008, 38 (471-503) :471-503

[15]

Oh C.H., 2006, INLEXT0601271

[16]

Podowski M.Z., 2009, P C SUP CO2 POW CYCL

[17]

Propp W. A., 1960180 INEI

[18] Corrosion of 9Cr Steel in CO2 at Intermediate Temperature I: Mechanism of Void-Induced Duplex Oxide Formation [J].

Rouillard, F. ;

Moine, G. ;

Martinelli, L. ;

Ruiz, J. C. .

OXIDATION OF METALS, 2012, 77 (1-2) :27-55

[19] Corrosion of 9Cr Steel in CO2 at Intermediate Temperature II: Mechanism of Carburization [J].

Rouillard, F. ;

Moine, G. ;

Tabarant, M. ;

Ruiz, J. C. .

OXIDATION OF METALS, 2012, 77 (1-2) :57-70

[20] Corrosion of 9Cr Steel in CO2 at Intermediate Temperature III: Modelling and Simulation of Void-induced Duplex Oxide Growth [J].

Rouillard, F. ;

Martinelli, L. .

OXIDATION OF METALS, 2012, 77 (1-2) :71-83

← 1 2 3 →