Microstructure, magnetic properties, and spontaneous magnetostriction of Tb0.2Pr0.8(Fe0.4Co0.6)x

The microstructure, magnetic properties and magnetostriction of Tb0.2Pr0.8(Fe0.4Co0.6)(infinity) (1.65 less than or equal to x less than or equal to 1.90) alloys has been studied. The Curie temperatures for the 1:2 and 1:3 phases decrease with increasing x, whereas the saturation magnetization increases with increasing cc. The remanent magnetization remains almost constant for all the samples and the coercivity decreases with increasing x. The spontaneous magnetostriction (lambda (111)) estimated from the splitting of the (440) lines is found to decrease with increasing x. The largest lambda (111) recorded for Tb0.2Pr0.8(Fe0.4Co0.6)(1.65) is 2900 ppm at room temperature.