Hot corrosion behavior of powder metallurgy Rene95 nickel-based superalloy in molten NaCl-Na2SO4 salts

被引：84
作者：
Lei Zheng [1 ,2 ]
Zhang Maicang [2 ]
Dong Jianxin [2 ]
机构：
[1] Univ Munster, Inst Mat Phys, D-48149 Munster, Germany
[2] Univ Sci & Technol Beijing, Sch Mat Sci & Engn, Dept Mat Sci, Beijing 10083, Peoples R China
来源：
MATERIALS & DESIGN | 2011年 / 32卷 / 04期
基金：
高等学校博士学科点专项科研基金; 中国国家自然科学基金;
关键词：
Non-ferros metals and alloys; Powder metallurgy; Corrosion; NI-BASED SUPERALLOY; ELECTROCHEMICAL IMPEDANCE; MECHANICAL-PROPERTIES; NA2SO4-NACL MELTS; MICROSTRUCTURE; OXIDATION; RESISTANCE; ALLOY; 900-DEGREES-C; SEGREGATION;
D O I：
10.1016/j.matdes.2010.11.067
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Hot corrosion behavior of powder metallurgy (PM) Rene95 Ni-based superalloy in molten 25%NaCl + 75%Na2SO4 salts at 650 degrees C, 700 degrees C and 750 degrees C are investigated by weight loss measurements, X-ray diffraction (XRD), scanning electron microscopy (SEM), and energy dispersive X-ray spectroscopy (EDS). Experimental results show that hot corrosion kinetics follow a square power law at 650 degrees C and linear power laws at 700 degrees C and 750 degrees C. The corrosion layers on the surface of PM Rene95 superalloy are detected to be mainly composed of Cr2O3, NiO, and Ni3S2 at each temperature. Besides, small amounts of NiCr2O4 at 700 degrees C and NaCl at 750 degrees C are observed respectively. Cross-sectional morphologies and corresponding elemental maps indicate that corrosion layers near scale/alloy interface are composed of oxides at 650 degrees C while duplex oxides and sulfides at 700 degrees C and 750 degrees C. According to these results, a cooperating mechanism of oxidation and sulfuration for hot corrosion of PM Rene95 Ni-based superalloy is confirmed. (C) 2010 Elsevier Ltd. All rights reserved.
引用
收藏
页码：1981 / 1989
页数：9
相关论文
共 43 条
[1]   ADVANCED MATERIALS FOR AIRCRAFT ENGINE APPLICATIONS [J].
BACKMAN, DG ;
WILLIAMS, JC .
SCIENCE, 1992, 255 (5048) :1082-1087
[2]   Improvement of high temperature oxidation and corrosion resistance of superalloy IN-738LC by pack cementation [J].
Bai, CY ;
Luo, YJ ;
Koo, CH .
SURFACE & COATINGS TECHNOLOGY, 2004, 183 (01) :74-88
[3]   Preparation and hot corrosion behaviour of an Al-gradient NiCoCrAlYSiB coating on a Ni-base superalloy [J].
Bao, Z. B. ;
Wang, Q. M. ;
Li, W. Z. ;
Liu, X. ;
Gong, J. ;
Xiong, T. Y. ;
Sun, C. .
CORROSION SCIENCE, 2009, 51 (04) :860-867
[4]   Oxidation-assisted creep damage in a wrought nickel-based superalloy: Experiments and modelling [J].
Chateau, E. ;
Remy, L. .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2010, 527 (7-8) :1655-1664
[5]   Hot corrosion behavior of Ni-base alloys in a molten salt under an oxidizing atmosphere [J].
Cho, Soo-Haeng ;
Hur, Jin-Mok ;
Seo, Chung-Seok ;
Yoon, Ji-Sup ;
Park, Seong-Won .
JOURNAL OF ALLOYS AND COMPOUNDS, 2009, 468 (1-2) :263-269
[6]  
Cook R. H., 1974, International Metallurgical Reviews, V19, P199, DOI 10.1179/095066074790136971
[7]   A comparative study of oxidation and hot corrosion of a cast nickel base superalloy in different corrosive environments [J].
Deb, D ;
Iyer, SR ;
Radhakrishnan, VM .
MATERIALS LETTERS, 1996, 29 (1-3) :19-23
[8]   Interfacial segregation and cosegregation behaviour in a nickel-base alloy 718 [J].
Dong, JX ;
Zhang, MC ;
Xie, XS ;
Thompson, RG .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2002, 328 (1-2) :8-13
[9]   Solidification of high-refractory ruthenium-containing superalloys [J].
Feng, Q ;
Nandy, TK ;
Tin, S ;
Pollock, TM .
ACTA MATERIALIA, 2003, 51 (01) :269-284
[10]   Corrosion performance of heat resistant alloys in Na2SO4-V2O5 molten salts [J].
Gonzalez-Rodriguez, J. G. ;
Haro, S. ;
Martinez-Villafane, A. ;
Salinas-Bravo, V. M. ;
Porcayo-Calderon, J. .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2006, 435 :258-265
12345