Influences of Ag addition to Sn-58Bi solder on SnBi/Cu interfacial reaction

被引：69
作者：
Hu, F. Q. [1 ]
Zhang, Q. K. [1 ]
Jiang, J. J. [1 ]
Song, Z. L. [1 ]
机构：
[1] Chinese Acad Sci, Ningbo Inst Mat Technol & Engn, Ningbo 315201, Zhejiang, Peoples R China
来源：
MATERIALS LETTERS | 2018年 / 214卷
关键词：
SnBi solder; Bi segregation; Ag addition; Interfacial embrittlement; Deformation and fracture; Interface; MECHANICAL-PROPERTIES; ALLOYING SUBSTRATE; TENSILE PROPERTIES; BI SEGREGATION; JOINTS; EMBRITTLEMENT; TEMPERATURE; MELT;
D O I：
10.1016/j.matlet.2017.11.127
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
In this study, the influences of Ag addition to Sn-58Bi solder on SnBi/Cu interfacial reaction and fracture behavior of the aged SnBiAg/Cu solder joints were investigated. The results reveal that the Ag element in the solder can diffuse into the Cu substrate during the soldering and aging process, forming a Cu-Ag alloy layer around the joint interface. The Bi segregation was not observed at the aged SnBiAg/Cu interface, and the embrittlement will not occur at the aged SnBiAg/Cu solder joints once the Bi segregation was restrained. (C) 2017 Elsevier B.V. All rights reserved.
引用
收藏
页码：142 / 145
页数：4
相关论文
共 50 条
  • [21] Influences of Ni addition into Cu-xNi alloy on the microstructure evolution and mechanical property of Sn-58Bi/Cu-xNi solder joint
    Cheng, Jinxuan
    Hu, Xiaowu
    Li, Qinglin
    Jiang, Xiongxin
    APPLIED PHYSICS A-MATERIALS SCIENCE & PROCESSING, 2020, 126 (04):
  • [22] Effects of Ce Addition on the Microstructure and Mechanical Properties of Sn-58Bi Solder Joints
    Tung-Han Chuang
    Hsing-Fei Wu
    Journal of Electronic Materials, 2011, 40 : 71 - 77
  • [23] Effects of Ce Addition on the Microstructure and Mechanical Properties of Sn-58Bi Solder Joints
    Chuang, Tung-Han
    Wu, Hsing-Fei
    JOURNAL OF ELECTRONIC MATERIALS, 2011, 40 (01) : 71 - 77
  • [24] Microstructure and Property Changes in Cu/Sn-58Bi/Cu Solder Joints during Thermomigration
    Shen, Yu-An
    Zhou, Shiqi
    Li, Jiahui
    Tu, K. N.
    Nishikawa, Hiroshi
    2019 IEEE 69TH ELECTRONIC COMPONENTS AND TECHNOLOGY CONFERENCE (ECTC), 2019, : 2003 - 2008
  • [25] Effects of CuZnAl Particles on Properties and Microstructure of Sn-58Bi Solder
    Yang, Fan
    Zhang, Liang
    Liu, Zhi-quan
    Zhong, Su Juan
    Ma, Jia
    Bao, Li
    MATERIALS, 2017, 10 (05)
  • [26] Reliability of Graphene Nanosheets-Reinforbed Sn-58Bi/Cu Solder Joints
    Jiang Nan
    Zhang Liang
    Xu Kaikai
    Wang Fengjiang
    Long Weimin
    RARE METAL MATERIALS AND ENGINEERING, 2021, 50 (07) : 2293 - 2299
  • [27] Improving tensile and fatigue properties of Sn-58Bi/Cu solder joints through alloying substrate
    Zhang, QingKe
    Zou, HeFei
    Zhang, Zhe-Feng
    JOURNAL OF MATERIALS RESEARCH, 2010, 25 (02) : 303 - 314
  • [28] Influences of low In alloying and aging on microstructure and plastic deformation behavior of Sn-58Bi solder
    Zhang, He
    Zhang, Qingke
    Song, Zhenlun
    JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS, 2024, 35 (17)
  • [29] Effect of Zn Addition on Interfacial Reactions Between Sn-Bi Solder and Cu Substrate
    Mokhtari, Omid
    Zhou, Shiqi
    Chan, Y. C.
    Nishikawa, Hiroshi
    MATERIALS TRANSACTIONS, 2016, 57 (08) : 1272 - 1276
  • [30] Microstructure and mechanical properties of Sn-58Bi eutectic alloy with Cu/P addition
    Li, Mingmao
    Tang, Yingying
    Li, Zhaoxin
    Zhu, Mingbiao
    Wang, Wenjing
    MATERIALS RESEARCH EXPRESS, 2020, 7 (11)
12345