Hydrothermal stabilization by lanthanum of mixed metal oxides and noble metal catalysts for volatile organic compound removal

被引:77
作者
Ferrandon, M [1 ]
Björnbom, E [1 ]
机构
[1] Royal Inst Technol, Dept Chem Engn & Technol, Div Chem React Engn, SE-10044 Stockholm, Sweden
关键词
manganese oxides; copper oxide; platinum; palladium; lanthanum; naphthalene; carbon monoxide; methane; oxidation; deactivation; stabilization; sintering; TPR; XPS;
D O I
10.1006/jcat.2001.3185
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
Catalysts based on manganese or copper oxides, mixed with platinum or palladium, supported on alumina alone or doped with lanthanum were characterized by BET, XRD, SEM, HRTEM, TPR, and XPS and tested for the oxidation of a mixture of naphthalene, CO, and CH4 in air, CO2, and water. The catalysts were also aged at 900 degreesC for 300 h in 10% steam. La was found in a dispersed phase in the alumina washcoat both before and after aging. Fresh manganese oxide catalysts, calcined at 800 degreesC, contained mostly Mn2O3, while on fresh copper samples, surface Cu2+ species were prevalent. It was found that Mn and Cu were better dispersed onto the alumina washcoat in the presence of La and that La increased the saturation of copper into alumina. The reducibility by H-2 of copper was also lowered by La. After aging, only CuO appeared on the unpromoted Cu-based catalysts, whereas, in the presence of La, the surface Cu2+ species were still present. The presence of active phases, particularly Cu and Pd, increased the formation of alpha -Al2O3 and the particle size of the alumina washcoat after aging. More than 60% of CuO reacted with alumina to form the spinel compound, CuAl2O4, whereas in presence of La, no spinel was formed. The addition of La onto fresh manganese-based catalysts led to an enhancement of the oxidation of CH4. The CuO-Pd/La-Al2O3 catalyst was found to be the most active catalyst for the oxidation of CO, C10H8, and CH4 before and after aging. (C) 2001 Academic Press.
引用
收藏
页码:148 / 159
页数:12
相关论文
共 77 条
  • [1] CHARACTERIZATION OF LANTHANIDE OXIDE-PROMOTED RHODIUM ALUMINA CATALYSTS
    ALVERO, R
    BERNAL, A
    CARRIZOSA, I
    ODRIOZOLA, JA
    [J]. INORGANICA CHIMICA ACTA, 1987, 140 (1-2) : 45 - 47
  • [2] BALTANAS MA, 1987, ACTA CHIM HUNG, V124, P341
  • [3] STABILIZATION OF ALUMINA BY ADDITION OF LANTHANUM
    BEGUIN, B
    GARBOWSKI, E
    PRIMET, M
    [J]. APPLIED CATALYSIS, 1991, 75 (01): : 119 - 132
  • [4] STUDIES OF URINARY TRACT INFECTIONS IN INFANCY AND CHILDHOOD .8. REINFECTION VS RELAPSE IN RECURRENT URINARY TRACT INFECTIONS . EVALUATION BY MEANS OF IDENTIFICATION OF INFECTING ORGANISMS
    BERGSTROM, T
    LINCOLN, K
    ORSKOV, F
    ORSKOV, I
    WINBERG, J
    [J]. JOURNAL OF PEDIATRICS, 1967, 71 (01) : 13 - +
  • [5] DISPERSION STUDIES ON THE SYSTEM LA2O3/GAMMA-AL2O3
    BETTMAN, M
    CHASE, RE
    OTTO, K
    WEBER, WH
    [J]. JOURNAL OF CATALYSIS, 1989, 117 (02) : 447 - 454
  • [6] INFLUENCE OF SURFACE-AREA AND ADDITIVES ON THE THERMAL-STABILITY OF TRANSITION ALUMINA CATALYST SUPPORTS .2. KINETIC-MODEL AND INTERPRETATION
    BURTIN, P
    BRUNELLE, JP
    PIJOLAT, M
    SOUSTELLE, M
    [J]. APPLIED CATALYSIS, 1987, 34 (1-2): : 239 - 254
  • [7] INFLUENCE OF SURFACE-AREA AND ADDITIVES ON THE THERMAL-STABILITY OF TRANSITION ALUMINA CATALYST SUPPORTS .1. KINETIC DATA
    BURTIN, P
    BRUNELLE, JP
    PIJOLAT, M
    SOUSTELLE, M
    [J]. APPLIED CATALYSIS, 1987, 34 (1-2): : 225 - 238
  • [8] Carol L. A., 892040 SAE
  • [9] CENTI G, 1995, J CATAL, V151, P75
  • [10] EFFECTS OF THE ADDITION OF LANTHANA ON THE THERMAL-STABILITY OF ALUMINA-SUPPORTED PALLADIUM
    CHOU, TY
    LEU, CH
    YEH, CT
    [J]. CATALYSIS TODAY, 1995, 26 (01) : 53 - 58