Preparation of calcium sulfoaluminate-belite cement from marble sludge waste

被引：77
作者：
El-Alfi, E. A. [1 ]
Gado, R. A. [1 ]
机构：
[1] Natl Res Ctr, Ceram & Bldg Mat Dept, Cairo 12311, Egypt
来源：
CONSTRUCTION AND BUILDING MATERIALS | 2016年 / 113卷
关键词：
Marble sludge waste; Environmentally cement; Low-energy cement; Sulfoaluminate-belite cement; Ettringite; FLY-ASH; PERFORMANCE; HYDRATION; SULFATE; CLINKER; RICH;
D O I：
10.1016/j.conbuildmat.2016.03.103
中图分类号：
TU [建筑科学];
学科分类号：
0813 ;
摘要：
Marble sludge waste was used as a major cement raw material in sintering sulfoaluminate cement clinker successfully in the laboratory. The influences of raw mix composition as well as different burning temperatures were investigated. Starting materials and prepared cement were characterized through different techniques including; Fourier transform infrared spectroscopy (FIR); X-ray diffraction (XRD) and scanning electron microscopy (SEM). The results reveal that calcium sulfoaluminate-belite cement can be produced by burning a raw mixture contains in weight percent (25% kaolin, 20% gypsum and 55% marble sludge waste) at firing temperature ranging between 1200 and 1250 degrees C. (C) 2016 Elsevier Ltd. All rights reserved.
引用
收藏
页码：764 / 772
页数：9
相关论文
共 49 条
  • [1] ADLER HH, 1962, AM MINERAL, V47, P700
  • [2] [Anonymous], 2010, SYNTHESIS CALCIUM SU
  • [3] [Anonymous], C202000 ASTM
  • [4] [Anonymous], 2014, INT J CHEMTECH RES
  • [5] [Anonymous], ASTMC109C109M
  • [6] Aranda MAG, 2013, WOOD PUBL SER CIVIL, P488, DOI 10.1533/9780857098993.4.488
  • [7] Sulfoaluminate-belite cement from low-calcium fly ash and sulfur-rich and other industrial by-products
    Arjunan, P
    Silsbee, MR
    Roy, DM
    [J]. CEMENT AND CONCRETE RESEARCH, 1999, 29 (08) : 1305 - 1311
  • [8] Baltaks K., 2007, MAT SCI POLAND, V25
  • [9] Baltakys K., 2007, MAT SCI POLAND, V25
  • [10] Berekta J., 1993, CEMENT CONCRETE RES, V26, P1673
12345