Effects of Different Barium Compounds on the Corrosion Resistance of Andalusite-Based Low-Cement Castables in Contact with Molten Al-Alloy

An experimental study was conducted to investigate the interfacial phenomena between an Al alloy and andalusite low-cement castables (LCCs) containing fixed contents of barium compounds (BaO, BaSO4, and BaCO3) at 1123 K and 1433 K (850 A degrees C and 1160 A degrees C) using the Alcoa cup test. Interfacial reaction products and phases formed during heat treatment of the refractory samples were characterized using scanning electron microscopy (SEM) coupled with energy dispersive spectrometry (EDS) and X-ray diffraction analysis (XRD). The addition of both BaO and BaSO4 led to a significant reduction of alloy penetration into the refractory. Hexa-celsian formation was observed in both these refractories, which drastically increased their corrosion resistance. Barite decomposition was observed at 1373 K (1100 A degrees C) in the presence of alumina and silica, which was the precursor for hexa-celsian formation. Barium silicates were formed in all samples containing additives; however, this did not have any major influence on the corrosion resistance. Solidified eutectics of BaSi2 and alpha-BaAl2Si2 formed in all these samples, which acted as an interfacial barrier that prevented additional molten aluminum penetration; however, the positive effect of intermetallic formation was offset by glassy phase formation in samples containing BaCO3 as the additive.