Effect of High Rotational-Speed Friction-Stir Welding on Microstructure and Properties of Welded Joints of 6061-T6 Al Alloy Ultrathin Plate

The butt joint of an Al alloy ultrathin plate with a thickness of 0.5 mm is realized by a high rotational-speed friction-stir welding process. It overcomes the welding difficulty that the ultrathin plate is often torn, and it cannot be formed by conventional friction-stir welding. The results show that the weld surface is well-formed at a high-rotational speed (more than 8000 rpm), and there are no obvious defects in each area of the joint section. The nugget zone (NZ) is a recovery recrystallization structure dominated by large-angle grain boundaries, with a grain size of about 4.9 mu m. During grain growth, the texture is randomly and uniformly distributed, and the strength is balanced. The microhardness of the NZ increases significantly with the increase in rotational speed, and the fluctuation range of hardness value is small. The NZ beta-Mg2Si is finer and significantly less than the base metal (BM). The heat dissipation of the thin plate is fast, so a Cu plate is used as the backing plate to slow down the steep temperature-drop process in the weld area. Compared with a low rotational speed, the precipitation amount of brittle phase Al-Cu-Mg-Cr and Al-Fe-Si-Mn is significantly reduced, which is conducive to improving the mechanical properties of the joint. At a high rotational speed, 12,000 rpm, the best tensile strength of the joint is 220 MPa, which is about 76% of the BM (290 MPa), and the highest elongation is 9.3%, which is about 77.5% of the BM (12%). The fracture mode of the joint is a typical plastic fracture.