Shear bond strength of metallic brackets photo-activated with light-emitting diode (LED) at different exposure times

被引:4
|
作者
Rego, Emanuel Braga [1 ]
Romano, Fabio Lourenco [1 ]
机构
[1] Univ Estadual Campinas, UNICAMP, Piracicaba Dent Sch, Campinas, Brazil
关键词
visible light; orthodontic brackets; shear strength;
D O I
10.1590/S1678-77572007000500007
中图分类号
R78 [口腔科学];
学科分类号
1003 ;
摘要
The purpose of this study was to compare the shear bond strength of orthodontic metallic brackets photo-activated with two different light-curing sources at different exposure times: halogen light (XL 1500, 3M ESPE) and LED light (Ortholux, 3M Unitek). Sixty bovine permanent lower incisors were inserted into PVC tubes containing plaster. The buccal surfaces were cleaned with pumice and water, and then etched with 37% phosphoric acid gel. The XT Primer bonding agent (3M Unitek) was applied to the enamel surfaces and the metallic pre-coated brackets (Transbond APC II system, 3M Unitek) were attached to upper central incisors. The teeth were randomly divided into four groups (n=15). In Group I (Control), halogen light was used for 40 seconds, while in Groups II, III, and IV were light-cured with LED light unit for 40, 10, and 5 seconds, respectively. The teeth were stored in distilled water at. 37 degrees C for 24 hours. The brackets were submitted to shear bond strength test in universal testing machine (Instron) at a crosshead speed of 0.5 mm/minute. Shear bond strength means (MPa) were 4.87 for Group I; 5.89 for Group II; 4.83 for Group III, and 4.39 for Group IV. Tukey's test detected no statistically significant differences among the groups regarding the shear bond strength (p>0.05). Neither of the types of light-curing sources or exposure times influenced the shear bond strength of metallic brackets.
引用
收藏
页码:412 / 415
页数:4
相关论文
共 50 条
  • [31] Effects of ultrasonic instrumentation with different scaler-tip angulations on the shear bond strength and bond failure mode of metallic orthodontic brackets
    Bonetti, Giulio Alessandri
    Parenti, Serena Incerti
    Ippolito, Daniela Rita
    Gatto, Maria Rosaria
    Checchi, Luigi
    KOREAN JOURNAL OF ORTHODONTICS, 2014, 44 (01) : 44 - 49
  • [32] Shear bond strength between gold alloy and orthodontic metal bracket using light emitting diode curing light
    Jung, Min-Ho
    Chung, Shin-Hye
    Shon, Won-Jun
    KOREAN JOURNAL OF ORTHODONTICS, 2010, 40 (01) : 27 - 33
  • [33] Effect of Different Light-Emitting Diode (LED) Lights on the Behavior and Habits of Scopulasub punctaria Herrichet Schaeffer
    Qiao, Li
    Guo, Shibao
    Jin, Yinli
    Wang, Chunsheng
    Yin, Jian
    Geng, Shubao
    JOURNAL OF BIOBASED MATERIALS AND BIOENERGY, 2021, 15 (02) : 203 - 209
  • [34] Comparison of the shear bond strength of new and recycled metallic brackets using different adhesive materials. An in vitro study
    Ibarra, R. Nicole
    Saez, Mackarena
    Rojas, Victor
    Oyonarte, Rodrigo
    EUROPEAN ORAL RESEARCH, 2023, 57 (02) : 96 - 102
  • [35] Effects of 445-nm Diode Laser-Assisted Debonding of Metallic Brackets on Shear Bond Strength and Enamel Surface Morphology
    Knaup, Thomas
    Korbmacher-Steiner, Heike
    Braun, Andreas
    Wenzler, Johannes-Simon
    Knaup, Isabel
    Stein, Steffen
    PHOTOBIOMODULATION PHOTOMEDICINE AND LASER SURGERY, 2020, 38 (03) : 160 - 166
  • [36] Orthodontic bracket shear bond strengths produced by two high-power light-emitting diode modes and halogen light
    Türkkahraman, H
    Küçükesmen, HC
    ANGLE ORTHODONTIST, 2005, 75 (05) : 854 - 857
  • [37] LED omics in Rocket Salad (Diplotaxis tenuifolia): Comparative Analysis in Different Light-Emitting Diode (LED) Spectrum and Energy Consumption
    Tsaballa, Aphrodite
    Xanthopoulou, Aliki
    Sperdouli, Ilektra
    Bantis, Filippos
    Boutsika, Anastasia
    Chatzigeorgiou, Ioanna
    Tsaliki, Eleni
    Koukounaras, Athanasios
    Ntinas, Georgios K.
    Ganopoulos, Ioannis
    PLANTS-BASEL, 2023, 12 (06):
  • [38] Effect of curing time on the bond strength of a bracket-bonding system cured with a light-emitting diode or plasma arc light
    Dall'Igna, Carine Maccarini
    Marchioro, Ernani Menezes
    Spohr, Ana Maria
    Mota, Eduardo Goncalves
    EUROPEAN JOURNAL OF ORTHODONTICS, 2011, 33 (01) : 55 - 59
  • [39] COMPARISON IN SHEAR BOND STRENGTH OF ORTHODONTIC BRACKETS BETWEEN 5 BONDING SYSTEMS RELATED TO DIFFERENT ETCHING TIMES - AN INVITRO STUDY
    SURMONT, P
    DERMAUT, L
    MARTENS, L
    MOORS, M
    AMERICAN JOURNAL OF ORTHODONTICS AND DENTOFACIAL ORTHOPEDICS, 1992, 101 (05) : 414 - 419
  • [40] Effect of exposure to a light-emitting diode (LED) on the physicochemical characteristics of natural latex biomembranes used to treat diabetic ulcers
    Santana T.F.
    Oliveira R.H.M.
    dos Santos L.E.
    Lima E.P.N.
    Faria S.S.
    Fonseca M.A.M.
    da Silva J.R.
    Tatmatsu-Rocha J.C.
    Gomes M.M.F.
    Fleury Rosa M.F.
    Fleury Rosa S.S.R.
    Carneiro M.L.B.
    Research on Biomedical Engineering, 2022, 38 (3) : 901 - 911