Backward rectifying and forward Schottky behavior at Au/Nb-1.0 wt %-doped SrTiO3 interface

被引：20

作者：

Cui, Yimin ^{[1
]}

Wang, Rongming ^{[1
]}

机构：

[1] Beijing Univ Aeronaut & Astronaut, Sch Sci, Beijing 100083, Peoples R China

来源：

APPLIED PHYSICS LETTERS | 2007年 / 91卷 / 23期

基金：

中国国家自然科学基金;

关键词：

D O I：

10.1063/1.2823583

中图分类号：

O59 [应用物理学];

学科分类号：

摘要：

The Au/Nb-1.0 wt %-doped SrTiO3 junctions were successfully fabricated by magnetic controlled sputtering and annealing process. Backward diodelike behaviors were observed in as-prepared junction and the one annealed at 350 degrees C. Transition to Schottky behavior was found in the junction annealed at 750 degrees C; the Schottky junction shows linear capacitance-voltage (C-2-V) relationship in the reverse condition with barrier heights determined to be 1.6 eV. The results of current-voltage (I-V) measurements reveal that high temperature annealing can alter interface barrier and thereby ameliorate the stability of leakage current remarkably. (c) 2007 American Institute of Physics.

引用

页数：3

共 50 条

[41] Fabrication and transport properties of ZnO/Nb-1 wt %-doped SrTiO3 epitaxial heterojunctions [J].

Wu, Yunlong ;

Zhang, Liuwan ;

Xie, Guanlin ;

Zhu, Jia-Lin ;

Chen, Yonghai .

APPLIED PHYSICS LETTERS, 2008, 92 (01)

[42] Ferroelectric memory resistive behavior in BaTiO3/Nb doped SrTiO3 heterojunctions [J].

Singh, Pooja ;

Rout, P. K. ;

Singh, Manju ;

Rakshit, R. K. ;

Dogra, Anjana .

THIN SOLID FILMS, 2017, 643 :60-64

[43] w Microstructural studies on the reoxidation behavior of Nb-doped SrTiO3 ceramics [J].

Rahmati, B ;

Fleig, J ;

Bischoff, E ;

Sigle, W ;

Maier, J ;

Rühle, A .

JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2005, 25 (12) :2211-2214

[44] Good rectifying characteristic in p-n junctions composed of La0.67Ca0.33MnO3-δ/Nb-0.7 wt %-doped SrTiO3 [J].

Hu, FX ;

Gao, J ;

Sun, JR ;

Shen, BG .

APPLIED PHYSICS LETTERS, 2003, 83 (09) :1869-1871

[45] Rectifying characteristics and magnetoresistance in La0.9Sr0.1MnO3/Nb-doped SrTiO3 heterojunctions [J].

Luo, Z. ;

Gao, J. .

MATERIALS SCIENCE AND ENGINEERING B-SOLID STATE MATERIALS FOR ADVANCED TECHNOLOGY, 2007, 144 (1-3) :109-112

[46] Temperature-dependent resistive switching behavior in the structure of Au/Nb:SrTiO3/Ti [J].

Shen, J. X. ;

Qian, H. Q. ;

Wang, G. F. ;

An, Y. H. ;

Li, P. G. ;

Zhang, Y. ;

Wang, S. L. ;

Chen, B. Y. ;

Tang, W. H. .

APPLIED PHYSICS A-MATERIALS SCIENCE & PROCESSING, 2013, 111 (01) :303-308

[47] Temperature-dependent resistive switching behavior in the structure of Au/Nb:SrTiO3/Ti [J].

J. X. Shen ;

H. Q. Qian ;

G. F. Wang ;

Y. H. An ;

P. G. Li ;

Y. Zhang ;

S. L. Wang ;

B. Y. Chen ;

W. H. Tang .

Applied Physics A, 2013, 111 :303-308

[48] Impact of interfacial effects on ferroelectric resistance switching of Au/BiFeO3/Nb:SrTiO3(100) Schottky junctions [J].

He, Shumin ;

Liu, Guolei ;

Zhu, Yinlian ;

Ma, Xiuliang ;

Sun, Jirong ;

Kang, Shishou ;

Yan, Shishen ;

Chen, Yanxue ;

Mei, Liangmo ;

Jiao, Jun .

RSC ADVANCES, 2017, 7 (37) :22715-22721

[49] Electric field penetration in Au/Nb: SrTiO3 Schottky junctions probed by bias-dependent internal photoemission [J].

Hikita, Y. ;

Kawamura, M. ;

Bell, C. ;

Hwang, H. Y. .

APPLIED PHYSICS LETTERS, 2011, 98 (19)

[50] Non-ohmic behavior of Nb-doped SrTiO3 grain boundary layers [J].

Kim, SH ;

Kim, HT ;

Byun, JD ;

Kim, YH .

JOURNAL OF THE KOREAN PHYSICAL SOCIETY, 1998, 32 :S1146-S1148

← 1 2 3 4 5 →