Backward rectifying and forward Schottky behavior at Au/Nb-1.0 wt %-doped SrTiO3 interface

被引：20

作者：

Cui, Yimin ^{[1
]}

Wang, Rongming ^{[1
]}

机构：

[1] Beijing Univ Aeronaut & Astronaut, Sch Sci, Beijing 100083, Peoples R China

来源：

APPLIED PHYSICS LETTERS | 2007年 / 91卷 / 23期

基金：

中国国家自然科学基金;

关键词：

D O I：

10.1063/1.2823583

中图分类号：

O59 [应用物理学];

学科分类号：

摘要：

The Au/Nb-1.0 wt %-doped SrTiO3 junctions were successfully fabricated by magnetic controlled sputtering and annealing process. Backward diodelike behaviors were observed in as-prepared junction and the one annealed at 350 degrees C. Transition to Schottky behavior was found in the junction annealed at 750 degrees C; the Schottky junction shows linear capacitance-voltage (C-2-V) relationship in the reverse condition with barrier heights determined to be 1.6 eV. The results of current-voltage (I-V) measurements reveal that high temperature annealing can alter interface barrier and thereby ameliorate the stability of leakage current remarkably. (c) 2007 American Institute of Physics.

引用

页数：3

共 50 条

[31] Rectifying I-V characteristic of LiNbO3/Nb-doped SrTiO3 heterojunction [J].

Guo, S. M. ;

Zhao, Y. G. ;

Xiong, C. M. ;

Lang, P. L. .

APPLIED PHYSICS LETTERS, 2006, 89 (22)

[32] Electrical properties of a Ba1-xKxBiO3Nb-doped SrTiO3 Schottky junction [J].

Suzuki, S ;

Yamamoto, T ;

Suzuki, H ;

Kawaguchi, K ;

Takahashi, K ;

Yoshisato, Y .

PHYSICA C, 1997, 282 :2501-2502

[33] Modulation of rectifying behaviour by oxygen contents in La0.5Sr0.5CoO3-δ/0.7 wt% Nb-doped SrTiO3 heterojunctions [J].

Li, G. ;

Yao, Y. P. ;

Hou, Y. ;

Zhou, T. F. ;

Li, X. G. .

JOURNAL OF PHYSICS D-APPLIED PHYSICS, 2009, 42 (06)

[34] Rectifying characteristics and tunable magnetoresistance in heterojunctions of La0.9Hf0.1MnO3/0.05 wt.% Nb-doped SrTiO3 [J].

Qi, Yaping ;

Liu, Xiangbo ;

Ni, Hao ;

Zheng, Ming ;

Chen, Liping ;

Wang, Lin ;

Jiang, Yucheng ;

Zhao, Meng ;

Gao, Ju .

INTERNATIONAL JOURNAL OF MODERN PHYSICS B, 2017, 31 (25)

[35] Colossal dielectric behavior of Nb-doped SrTiO3 single crystal [J].

Liu, Xudong ;

Ma, Hanshu ;

Hu, Yongqi ;

Lu, Jiahui ;

Wang, Lei .

JOURNAL OF CRYSTAL GROWTH, 2024, 642

[36] Interface resistance switching characteristics of metal/Nb-doped SrTiO3 junctions [J].

Park, Chanwoo ;

Kim, Dong-Wook .

JOURNAL OF THE KOREAN PHYSICAL SOCIETY, 2007, 50 (05) :1294-1297

[37] Electrical investigation of Nb-doped SrTiO3 interface using impedance spectroscopy [J].

Kim, SH ;

Park, JG ;

Kim, Y ;

Kim, DY .

JOURNAL OF MATERIALS SCIENCE LETTERS, 2000, 19 (21) :1955-1957

[38] Interface State Effects on Resistive Switching Behaviors of Pt/Nb-Doped SrTiO3 Single-Crystal Schottky Junctions [J].

Bourim, El Mostafa ;

Kim, Yoonjung ;

Kim, Dong-Wook .

ECS JOURNAL OF SOLID STATE SCIENCE AND TECHNOLOGY, 2014, 3 (07) :N95-N101

[39] Electric field modulation of tunneling anisotropic magnetoresistance across the Schottky interface of Ni/Nb-doped SrTiO3 at room temperature [J].

Das, A. ;

Goossens, V. M. ;

Goossens, A. S. ;

Banerjee, T. .

SPINTRONICS XI, 2018, 10732

[40] Probing hot electron transport across an epitaxial Schottky interface of SrRuO3/Nb:SrTiO3 [J].

Roy, S. ;

Kamerbeek, A. M. ;

Rana, K. G. ;

Parui, S. ;

Banerjee, T. .

APPLIED PHYSICS LETTERS, 2013, 102 (19)

← 1 2 3 4 5 →