Backward rectifying and forward Schottky behavior at Au/Nb-1.0 wt %-doped SrTiO3 interface

被引：20

作者：

Cui, Yimin ^{[1
]}

Wang, Rongming ^{[1
]}

机构：

[1] Beijing Univ Aeronaut & Astronaut, Sch Sci, Beijing 100083, Peoples R China

来源：

APPLIED PHYSICS LETTERS | 2007年 / 91卷 / 23期

基金：

中国国家自然科学基金;

关键词：

D O I：

10.1063/1.2823583

中图分类号：

O59 [应用物理学];

学科分类号：

摘要：

The Au/Nb-1.0 wt %-doped SrTiO3 junctions were successfully fabricated by magnetic controlled sputtering and annealing process. Backward diodelike behaviors were observed in as-prepared junction and the one annealed at 350 degrees C. Transition to Schottky behavior was found in the junction annealed at 750 degrees C; the Schottky junction shows linear capacitance-voltage (C-2-V) relationship in the reverse condition with barrier heights determined to be 1.6 eV. The results of current-voltage (I-V) measurements reveal that high temperature annealing can alter interface barrier and thereby ameliorate the stability of leakage current remarkably. (c) 2007 American Institute of Physics.

引用

页数：3

共 50 条

[21] Backward-Like Rectifying Behavior of La1.85Sr0.15CuO4/Nb:SrTiO3 Heterojunctions [J].

L. M. Chen ;

B. Xu ;

Z. P. Chen ;

P. Chen ;

R. Zhang .

Journal of Superconductivity and Novel Magnetism, 2012, 25 :983-988

[22] Temperature-dependent polarity reversal in Au/Nb:SrTiO3 Schottky junctions [J].

Susaki, T. ;

Kozuka, Y. ;

Tateyama, Y. ;

Hwang, H. Y. .

PHYSICAL REVIEW B, 2007, 76 (15)

[23] Modulation of resistance switching in Au/Nb:SrTiO3 Schottky junctions by ambient oxygen [J].

Buzio, R. ;

Gerbi, A. ;

Gadaleta, A. ;

Anghinolfi, L. ;

Bisio, F. ;

Bellingeri, E. ;

Siri, A. S. ;

Marre, D. .

APPLIED PHYSICS LETTERS, 2012, 101 (24)

[24] Schottky barrier formation at the Fe3O4/Nb:SrTiO3 interface [J].

Ziese, M ;

Köhler, U ;

Höhne, R ;

Bollero, A ;

Esquinazi, P .

JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 2005, 290 :1116-1119

[25] Electrochemical characterization and redox behavior of Nb-doped SrTiO3 [J].

Blennow, Peter ;

Hansen, Kent K. ;

Wallenberg, L. Reine ;

Mogensen, Mogens .

SOLID STATE IONICS, 2009, 180 (01) :63-+

[26] Rectifying properties and colossal magnetoresistance in La0.9Hf0.1MnO3/Nb-0.7 wt%-doped SrTiO3 heterojunction [J].

Wang, Lin ;

Wu, Zhenping ;

Jiang, Yucheng ;

Ren, Bing ;

Huang, Jian ;

Tang, Ke ;

Zhang, Wenzhu ;

Gao, Ju ;

Wang, Linjun .

EIGHTH INTERNATIONAL CONFERENCE ON THIN FILM PHYSICS AND APPLICATIONS, 2013, 9068

[27] Rectifying behavior and transport mechanisms of currents in Pt/BaTiO3/Nb:SrTiO3 structure [J].

Pan, R. K. ;

Zhang, T. J. ;

Wang, J. Z. ;

Ma, Z. J. ;

Wang, J. Y. ;

Wang, D. F. .

JOURNAL OF ALLOYS AND COMPOUNDS, 2012, 519 :140-143

[28] Rectifying characteristics and transport behavior of the La0.9Hf0.1MnO3/Nb-doped SrTiO3 heterojunction [J].

Wang, L. ;

Gao, J. .

JOURNAL OF APPLIED PHYSICS, 2009, 105 (07)

[29] The influence of interface contact condition on resistive switching of Au/Nb:SrTiO3 heterojunctions [J].

Li, Jialu ;

Guo, Wei ;

Qiao, Yadong ;

Yao, Li ;

He, Zhiquan ;

Wang, Fadi ;

Wang, Yuhang ;

Wang, Fengping .

APPLIED PHYSICS LETTERS, 2023, 123 (15)

[30] Rectifying current-voltage characteristics of BiFeO3/Nb-doped SrTiO3 heterojunction [J].

Yang, H. ;

Luo, H. M. ;

Wang, H. ;

Usov, I. O. ;

Suvorova, N. A. ;

Jain, M. ;

Feldmann, D. M. ;

Dowden, P. C. ;

DePaula, R. F. ;

Jia, Q. X. .

APPLIED PHYSICS LETTERS, 2008, 92 (10)

← 1 2 3 4 5 →