Shrinkage porosity and its alleviation by heavy reduction in continuously cast strand

被引:34
作者
Dong, Qipeng [1 ]
Zhang, Jiongming [1 ]
Wang, Bo [1 ]
Zhao, Xinkai [1 ]
机构
[1] Univ Sci & Technol Beijing, State Key Lab Adv Met, 30 Coll Rd, Beijing 100083, Peoples R China
基金
中国国家自然科学基金;
关键词
Porosity; Improvement; Heavy reduction; Experiment; Closure; FINITE-ELEMENT-ANALYSIS; HOT-ROLLING PROCESS; PREDICTION; EFFICIENCY; CRITERION; CLOSURE;
D O I
10.1016/j.jmatprotec.2016.07.007
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Heavy reduction process was proposed as a novel strategy to alleviate the porosity during strand continuous casting, and a few studies were performed to investigate the formation of shrinkage porosity and the effect of heavy reduction on the porosity. A simplified model was applied to quantitatively predict shrinkage porosity, about 2.7 mm in diameter in the experimental conditions was obtained. A series of plant trials, including single-roll heavy reduction and multi-roll heavy reduction, were performed to study the effect of the application on porosity. The heavy reduction process effectively alleviated the porosity in the billets, and large reduction and a high central solid fraction showed a large contribution to the alleviation. Traditional soft reduction was also conducted for comparison, and heavy reduction was found to be more effective than the soft reduction in the improvement on porosity. The morphology of porosity during reduction process was analyzed with numerical simulation. Both the closure index and hydrostatic stress proved the effective role of heavy reduction in the alleviation of porosity. (C) 2016 Elsevier B.V. All rights reserved.
引用
收藏
页码:81 / 88
页数:8
相关论文
共 24 条
[1]  
Araki K., 1999, KAWASAKI STEEL TECH, V40, P80
[2]   Prediction of Shrinkage Pore Volume Fraction Using a Dimensionless Niyama Criterion [J].
Carlson, Kent D. ;
Beckermann, Christoph .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2009, 40A (01) :163-175
[3]  
Chaaban M., 1977, P 17 INT MACH TOOL D, P633
[4]   Rigid-plastic finite element analysis of plastic deformation of porous metal sheets containing internal void defects [J].
Chen, Dyi-Cheng .
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2006, 180 (1-3) :193-200
[5]  
ENGSTROM G, 1983, SCAND J METALL, V12, P3
[6]  
Hiraki S., 2009, Mater. Jpn, P20
[7]   Internal reduction efficiency of continuously cast strand with liquid core [J].
Ito, Y ;
Yamanaka, A ;
Watanabe, T .
REVUE DE METALLURGIE-CAHIERS D INFORMATIONS TECHNIQUES, 2000, 97 (10) :1171-1176
[8]   FINITE-DIFFERENCE HEAT-TRANSFER MODELING FOR CONTINUOUS-CASTING [J].
LALLY, B ;
BIEGLER, L ;
HENEIN, H .
METALLURGICAL TRANSACTIONS B-PROCESS METALLURGY, 1990, 21 (04) :761-770
[9]   Internal void closure during the forging of large cast ingots using a simulation approach [J].
Lee, Y. S. ;
Lee, S. U. ;
Van Tyne, C. J. ;
Joo, B. D. ;
Moon, Y. H. .
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2011, 211 (06) :1136-1145
[10]   Investigation of reduction pretreatment process for continuous casting [J].
Li, Gaosheng ;
Yu, Wei ;
Cai, Qingwu .
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2016, 227 :41-48