Dielectric and piezoelectric properties of Na0.42K0.08K0.08Bi0.5TiO3 and Na0.45K0.05Bi0.5TiO3 ceramics

Na0.42KD0.08Bi0.5TiO3 and Na0.45K0.05Bi0.5TiO3 ceramics were fabricated by the solid-state reaction. The structures were determined by X-ray diffraction. Dielectric, ferroelectric and piezoelectric properties of the ceramics were measured and discussed. The ceramics have a single perovskite phase with rhombohedral. symmetry at room temperature. The thermal variations of the permittivity follow the law 1/epsilon - 1/epsilon(m) = C(T - T-m)(2) which is the character of typical relax ferroelectrics, when temperature is higher than the temperature of the maximum of dielectric constant (Tm). The depolarization. temperature (T-d) of spontaneous polarization is 215degreesC for Na0.45K0.05Bi0.5TiO3 and 152degreesC for Na0.42K0.08Bi0.5TiO3 respectively. There exist two different dielectric behaviors of the Na0.42K0.08Bi0.5TiO3 ceramic, without and after poling. Na0.45K0.05Bi0.5TiO3 possesses relatively high k(t) and T-d. The use device application has been indicated.