Solidification and Stabilization of Spent TBP/OK Organic Liquids in a Phosphate Acid-Based Geopolymer

被引：25

作者：

Dong, Teng ^{[1
,2
]}

Xie, Shuibo ^{[1
,2
]}

Wang, Jingsong ^{[1
]}

Zhao, Guodong ^{[2
]}

Song, Qingchun ^{[1
]}

机构：

[1] Univ South China, Pollut Control & Resource Recovery Technol Key La, Hengyang 421001, Hunan, Peoples R China

[2] Univ South China, Sch Resources Environm & Safety Engn, Hengyang 421001, Hunan, Peoples R China

来源：

SCIENCE AND TECHNOLOGY OF NUCLEAR INSTALLATIONS | 2020年 / 2020卷

关键词：

15;

D O I：

10.1155/2020/8094205

中图分类号：

TL [原子能技术]; O571 [原子核物理学];

学科分类号：

0827 ; 082701 ;

摘要：

A method for solidifying spent tributyl phosphate and kerosene (TBP/OK) organic liquids in a phosphate acid-based geopolymer (PAG) was investigated. The TBP/OK emulsion containing tween 80 (T80), TBP/OK organic liquids, and H3PO4 was prepared. The TBP/OK emulsion was mixed with metakaolin to obtain solidified TBP/OK forms (SPT). The compressive strength of the SPT was up to 59.19 MPa when the content of TBP/OK was 18%. The loss of compressive strength of SPT was less than 10% after immersion and less than 25% after freeze-thaw treatment. The final setting time was 40.0 h, and the shrinkage of SPT was nearly 3%. The leaching test indicated that the release of TBP/OK from hardened SPT was limited. Characterization of SPT suggested that solidification of TBP/OK using PAG occurred by physical encapsulation.

引用

页数：7

共 15 条

[11] Mechanical and microstructural properties of metakaolin-based geopolymer cements from sodium waterglass and phosphoric acid solution as hardeners: A comparative study [J].

Tchakoute, Herve Kouamo ;

Ruscher, Claus Henning .

APPLIED CLAY SCIENCE, 2017, 140 :81-87

[12]

Yang N., 2000, The Handbook of Inorganic Matalloid Materials Atlas, Vfirst

[13]

[张书政 Zhang Shuzheng], 2003, [材料科学与工程学报, Journal Materials Science and Engineering], V21, P430

[14] Solidification of spent radioactive organic solvent by sulfoaluminate and Portland cements [J].

Zhang, Wenfeng ;

Li, Junfeng ;

Wang, Jianlong .

JOURNAL OF NUCLEAR SCIENCE AND TECHNOLOGY, 2015, 52 (11) :1362-1368

[15]

Zhuying C., 1991, AT ENERGY SCI TECHNO, V2, P74

← 1 2 →