Effect of ammonium chloride on corrosion behavior of Ni-based alloys and stainless steel in supercritical water gasification process

被引：41

作者：

Yang, Jianqiao ^{[1
]}

Wang, Shuzhong ^{[1
]}

Xu, Donghai ^{[1
]}

Guo, Yang ^{[1
,2
]}

Yang, Chuang ^{[1
]}

Li, Yanhui ^{[1
]}

机构：

[1] Xi An Jiao Tong Univ, Key Lab Thermo Fluid Sci & Engn, MOE, Xian 710049, Shaanxi, Peoples R China

[2] Xi An Jiao Tong Univ, Suzhou Acad, Suzhou 215123, Jiangsu, Peoples R China

来源：

INTERNATIONAL JOURNAL OF HYDROGEN ENERGY | 2017年 / 42卷 / 31期

基金：

中国国家自然科学基金;

关键词：

Ni-based alloy; Stainless steel; Supercritical water gasification; Ammonium chloride; Corrosion; AQUEOUS-SOLUTIONS; HIGH-TEMPERATURE; DISSOLVED HYDROGEN; OXIDE-FILM; NICKEL; MOLYBDENUM; OXIDATION; CHROMIUM; OXYGEN; PH;

D O I：

10.1016/j.ijhydene.2017.05.078

中图分类号：

O64 [物理化学（理论化学）、化学物理学];

学科分类号：

070304 ; 081704 ;

摘要：

The corrosion behavior of 316 SS and three Ni-based alloys 625, 600 and 800 was evaluated by exposing in SCW at 400 degrees C and 24 MPa with 6000 ppm NH4Cl for 70 h. Various of analytical techniques were used for corrosion analysis. 316 SS underwent severe corrosion attack for general corrosion, pitting corrosion and intergranular attack. Inconel 625 showed the best corrosion resistance in the test environment. Fe oxides and spinel were identified by XRD on all of the SCW-exposed samples. Trace amounts of NiO was also identified on the surface of samples, however, Ni was selectively dissolved and depleted in oxide films, and nickel ammine may form at the relatively low temperature during the heating and cooling process. (C) 2017 Hydrogen Energy Publications LLC. Published by Elsevier Ltd. All rights reserved.

引用

页码：19788 / 19797

页数：10

共 50 条

[21] Erosion-corrosion behavior of Nickel based alloys in supercritical water oxidation environment
Yang, Jianqiao
Wang, Shuzhong
Wang, Jiahuan
Wang, Jinlong
Zhang, Baoquan
Liu, Lu
Liu, Wei
Li, Yanhui
Xu, Donghai
JOURNAL OF SUPERCRITICAL FLUIDS, 2022, 187
[22] Modeling the Impact of Grain Size on Corrosion Behavior of Ni-Based Alloys in Molten Chloride Salt via Cellular Automata
Feng, Jinghua
Gao, Jianxi
Mao, Li
Bedell, Ryan
Liu, Emily
METALS, 2024, 14 (08)
[23] Effect of annealing and supercritical CO2 exposure at 750°C on the tensile properties of stainless steel and Ni-based structural alloys
Dryepondt, Sebastien N.
Lehmusto, Juho
Pint, Bruce A.
MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2022, 73 (04): : 497 - 512
[24] Effect of oxygen concentration on the corrosion behavior of Cr-coated Ni alloy in supercritical water oxidation environment
Yang, Jianqiao
Sun, Jiyuan
Bai, Shuyuan
Wu, Hao
Wang, Shuzhong
Li, Yanhui
Ma, Wenhao
Xu, Donghai
JOURNAL OF SUPERCRITICAL FLUIDS, 2022, 191
[25] Effect of low oxygen concentration on the oxidation behavior of Ni-based alloys 625 and 825 in supercritical water
Yang, Jianqiao
Wang, Shuzhong
Tang, Xingying
Wang, Yuzhen
Li, Yanhui
JOURNAL OF SUPERCRITICAL FLUIDS, 2018, 131 : 1 - 10
[26] Efficient and stable supercritical-water-synthesized Ni-based catalysts for supercritical water gasification
Li, Sha
Zhu, Bin
Wang, Wenju
Zhang, Houlei
Li, Qiang
JOURNAL OF SUPERCRITICAL FLUIDS, 2020, 160
[27] The corrosion behavior of AISI 310 stainless steel in thiosulfate ion containing saturated ammonium chloride solution
Kuo, HS
Chang, H
Tsai, WT
CORROSION SCIENCE, 1999, 41 (04) : 669 - 684
[28] High temperature corrosion behavior of Ni-based alloys
Soo-Haeng Cho
Seung-Chul Oh
Seong-Bin Park
Kwang-Mo Ku
Jong-Hyeon Lee
Jin-Mok Hur
Han-Soo Lee
Metals and Materials International, 2012, 18 : 939 - 949
[29] Under-deposit corrosion of Ni-based alloy 825 and Fe-Ni based alloy 800 in supercritical water oxidation environment
Yang, Jianqiao
Wang, Shuzhong
Li, Yanhui
Xu, Donghai
CORROSION SCIENCE, 2020, 167
[30] Corrosion resistance of stainless steel joints bonded with a Ni-based amorphous interlayer
Gonzalez-Sanchez, J.
Verduzco, J. A.
Lemus-Ruiz, Jose
Tellez, M. G.
Torres, R.
ANTI-CORROSION METHODS AND MATERIALS, 2007, 54 (02) : 68 - 73

← 1 2 3 4 5 →