Synthesis of black pigments containing chromium from leather sludge

The black ceramic pigments with spinel structure have been prepared by using Cr-rich leather sludge in this paper. The washed Cr-rich leather sludge calcined at 1100 degrees C for 1 h as chromium oxide precursor (named as CA) was mixed with an appropriate proportion of other industrial metallic oxides, followed synthesizing black ceramic pigment by sintering. Both non-washed and washed sludge fired at 1100 degrees C were characterized by X-ray fluorescence (XRF) in order to determine their chemical compositions and X-ray diffraction (XRD) analysis to confirm that CA mainly contains Cr2O3 crystal phase. The results show that CA could be used as a source of chromium to prepare black pigment. The crystalline phases of obtained pigments were characterized by XRD. Furthermore, the morphology as well as the composition of pigments was investigated by scanning electron microscopy (SEM) and energy dispersion spectroscopy (EDS). The color coordinates of pigments were examined and compared with the commercial pigments based on CEE-L* a* b* values measured using UV-vis spectroscopy. The obtained pigments sintered at 1200 degrees C with 35-55 wt% content of CA possess the excellent black spinel structure and color effect. Under optimized conditions, the pigment has low average spectral reflectance (7%). (C) 2015 Elsevier Ltd and Techna Group S.r.l. All rights reserved.