Recrystallization Law of Ti-IF Steel During Annealing Process

被引：0
作者：
Feng, Yanqing [1 ,2 ]
Gao, Zhiguo [2 ]
Wang, Fuming [1 ]
机构：
[1] Univ Sci & Technol Beijing, Beijing 100083, Peoples R China
[2] Baotou Iron & Steel Grp Co Ltd, Baotou, Peoples R China
来源：
NEW MATERIALS, APPLICATIONS AND PROCESSES, PTS 1-3 | 2012年 / 399-401卷
关键词：
Ti-IF steel; Annealing; Recrystallization; HIGH-STRENGTH STEELS; TEXTURE FORMATION; PRECIPITATION; BEHAVIOR;
D O I：
10.4028/www.scientific.net/AMR.399-401.2301
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Recrystallization law was investigated at different annealing processes. The results showed that the annealing temperature was a main effect factor on the properties of Ti-IF steel. Nominal recrystallization temperature of the samples was evaluated as 620 degrees C. Simulated batch annealing was performed by two-stage heating. Determined recrystallization temperature was 660 degrees C, the recrystallization of samples heated at 660 degrees C was completed in 68min. For 800 degrees C, the equiaxial recrystallized grains were obtained. Simulated continuous annealing by rapidly heating to different temperatures, samples were held for 100s and then cooled in air. Recrystallization nucleation was not observed until 660 degrees C. The occurrence of secondary recrystallization was observed at 900 degrees C.
引用
收藏
页码：2301 / +
页数：2
相关论文
共 50 条
  • [31] The Effect of Annealing Temperature on the Properties and Second-Phase Particles of 0.4mm Galvanized Ti-IF Steel
    Li, Feng
    Lv, Jiashun
    Yang, Honggang
    Zhou, Fang
    Zhang, Leng
    Wang, Endong
    MATERIALS ENGINEERING AND MECHANICAL AUTOMATION, 2014, 442 : 58 - +
  • [32] On the Issue of Recrystallization Annealing of Dynamo Steel
    Gubanov O.M.
    Burba V.S.
    Steel in Translation, 2023, 53 (10) : 851 - 857
  • [33] Microstructure and texture evolution during recrystallization of low-carbon steel sheets
    Zhuane, Dong-dong
    Wang, Lei-gang
    Huang, Yao
    Li, Xiao-min
    Zhang, Hua-yang
    Ren, De-wei
    JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL, 2017, 24 (01) : 84 - 90
  • [34] Effect of phosphorus contents on texture and grain boundary character for the annealing high strength Ti-IF steels
    Song, X. L.
    Peng, K.
    Zhang, P. P.
    Wu, J. Y.
    Zhou, J.
    Jia, J.
    Fan, L. X.
    ADVANCES IN MATERIALS AND MATERIALS PROCESSING, PTS 1-3, 2013, 652-654 : 929 - 933
  • [35] Fabrication of Porous Crystalline PLGA-PEG Induced by Swelling during the Recrystallization Annealing Process
    Dai, Jidong
    Tan, Xin
    Liang, Min
    Wei, Dandan
    Tao, Yinhua
    Ren, Pengfei
    Zhang, Tianzhu
    ACS BIOMATERIALS SCIENCE & ENGINEERING, 2021, 7 (12) : 5524 - 5531
  • [36] Recrystallization Behavior of 0.11% Ti-added Complex Phase Steel During Hot Compression
    Zhang, Mei
    Huang, Chao-bin
    Zeng, Wei-ming
    Fu, Ren-fu
    Li, Lin
    PHYSICAL AND NUMERICAL SIMULATION OF MATERIALS PROCESSING VII, 2013, 762 : 128 - +
  • [37] Monte Carlo modelling of recrystallization process in cold rolled IF-Ti steel
    Samet-Meziou, A
    Gerber, P
    Tarasiuk, J
    Baudin, T
    Penelle, R
    RECRYSTALLIZATION AND GRAIN GROWTH, PTS 1 AND 2, 2004, 467-470 : 665 - 670
  • [38] Orientation dependent intragranular stored energy in polycrystalline Ti-IF steel
    Castelnau, O
    Ungár, T
    Miroux, A
    Chauveau, T
    Bacroix, B
    EUROPEAN POWDER DIFFRACTION, PTS 1 AND 2, 2000, 321-3 : 720 - 725
  • [39] Recrystallization of Hot-Rolled 2A14 Alloy during Semisolid Temperature Annealing Process
    Liu, Yingze
    Jiang, Jufu
    Zhang, Ying
    Huang, Minjie
    Dong, Jian
    Wang, Ying
    MATERIALS, 2023, 16 (07)
  • [40] Study of the recrystallization and crystallographic texture evolution during final annealing of UNS 532304 Lean Duplex stainless steel
    Moura, A. N.
    Favarato, L. N. O.
    Itman Filho, A.
    Alcantara, C. M.
    Cunha, M. A.
    Oliveira, T. R.
    Machado, M. L. P.
    MATERIALS CHARACTERIZATION, 2017, 130 : 39 - 49
12345