Microstructure and mechanical properties of 15-5 PH stainless steel under different aging temperature

被引:5
作者
Jin, Chunhui [1 ]
Zhou, Honglin [2 ]
Lai, Yuan [1 ]
Li, Bei [1 ]
Zhang, Kewei [1 ]
Chen, Huiqin [1 ]
Zhao, Jinhua [1 ]
机构
[1] Taiyuan Univ Sci & Technol, Sch Mat Sci & Engn, Taiyuan 030024, Peoples R China
[2] Neusoft Med Sysems Co Ltd, Shenyang 110179, Peoples R China
关键词
15-5 PH stainless steel; aging process; strengthening mechanism; lath martensite; HARDENING BEHAVIOR; TRANSFORMATION; AUSTENITE; EVOLUTION; STRENGTH; LASER;
D O I
10.1051/metal/2021078
中图分类号
TF [冶金工业];
学科分类号
0806 ;
摘要
The influence of aging temperature on microstructure and mechanical properties of Cr15Ni5 precipitation hardening stainless steel (15-5 PH stainless steel) were investigated at aging temperature range of 440-610 degrees C. The tensile properties at ambient temperature of the 15-5 PH stainless steel processed by different aging temperatures were tested, and the microstructural features were further analyzed utilizing optical microscope (OM), transmission electron microscope (TEM), electron backscatter diffraction (EBSD) as well as X-ray diffraction (XRD), respectively. Results indicated the strength of the 15-5 PH stainless steel was firstly decreased with increment of aging temperature from 440 to 540 degrees C, and then increased with the increment of aging temperature from 540 to 610 degrees C. The strength and ductility were well matched at aging temperature 470 degrees C, and the yield strength, tensile strength as well as elongation were determined to be 1170 MPa, 1240 MPa and 24%, respectively. The microstructures concerning to different aging temperatures were overall confirmed to be lath martensite. The strengthening mechanisms induced by dislocation density and the second phase precipitation of Cu-enriched metallic compound under different aging temperatures were determined to be the predominant strengthening mechanisms controlling the variation trend of mechanical properties corresponding to different aging temperatures with respect to 15-5 PH stainless steel.
引用
收藏
页数:10
相关论文
共 27 条
[21]   Cracking due to Cu and Ni segregation in a 17-4 PH stainless steel piston rod [J].
Tian, Jialong ;
Wang, Wei ;
Yan, Wei ;
Jiang, Zhouhua ;
Shan, Yiyin ;
Yang, Ke .
ENGINEERING FAILURE ANALYSIS, 2016, 65 :57-64
[22]   Cu-Precipitation Strengthening in Ultrahigh-Strength Carburizing Steels [J].
Tiemens, Benjamin L. ;
Sachdev, Anil K. ;
Olson, Gregory B. .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2012, 43A (10) :3615-3625
[23]   EFFECTS OF AGING ON THE MICROSTRUCTURE OF 17-4 PH STAINLESS-STEEL [J].
VISWANATHAN, UK ;
BANERJEE, S ;
KRISHNAN, R .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1988, 104 :181-189
[24]   The spinodal decomposition in 17-4PH stainless steel subjected to long-term aging at 350 °C [J].
Wang, Jun ;
Zou, Hong ;
Li, Cong ;
Qiu, Shaoyu ;
Shen, Baoluo .
MATERIALS CHARACTERIZATION, 2008, 59 (05) :587-591
[25]   The effect of microstructural evolution on hardening behavior of type 17-4PH stainless steel in long-term aging at 350 °C [J].
Wang, Jun ;
Zou, Hong ;
Li, Cong ;
Qiu, Shao-yu ;
Shen, Bao-luo .
MATERIALS CHARACTERIZATION, 2006, 57 (4-5) :274-280
[26]   Relationship of microstructure transformation and hardening behavior of type 17-4 PH stainless steel [J].
Wang, Jun ;
Zou, Hong ;
Li, Cong ;
Zuo, Ruling ;
Qiu, Shaoyu ;
Shen, Baoluo .
JOURNAL OF UNIVERSITY OF SCIENCE AND TECHNOLOGY BEIJING, 2006, 13 (03) :235-239
[27]   Cu precipitation-me diate d formation of reverted austenite during ageing of a 15-5 PH stainless steel [J].
Zhou, Tao ;
Neding, Benjamin ;
Lin, Sen ;
Tseng, Jo-Chi ;
Hedstrom, Peter .
SCRIPTA MATERIALIA, 2021, 202