Magnetic and magnetoresistance properties of spin valves using epitaxial Fe3O4 (110) as the pinning layer -: art. no. 063903

Magnetic and magnetoresistance (MR) properties of spin valves composed of Co/Cu/Co/iron oxide layer were studied using epitaxial Fe3O4 (110) grown on MgO (110) as the pinning layer. It was confirmed from the in-plane magnetization curves that the epitaxial Fe3O4 (110) films have the easy axes along the < 110 > direction and the hard axes along the < 001 > direction. The spin valves composed of Co/Cu/Co/Fe3O4 (110) showed quite different MR curves depending upon the direction of the magnetic field applied in the plane of Fe3O4 (110). Butterflylike MR curves, which imply the difference in the coercive fields between the top and bottom Co layers, were observed when the field was applied along the < 001 > direction of Fe3O4. On the other hand, flat MR curves, which implied the difference of the saturation fields between top and bottom Co, were observed when the field was applied along the < 110 > direction of Fe3O4. The magnetization easy axis of Co layers might be perpendicular to that of Fe3O4. These magnetic and MR properties could be explained by assuming the 90 degrees coupling between the bottom Co and the Fe3O4 layers, and the ferromagnetic coupling (so-called Neel-type coupling) between the top and bottom Co layers. (c) 2005 American Institute of Physics.