Microstructure and strength of oxidation-bonded porous silicon nitride ceramics

被引：1
|
作者：
Ding, Shuqiang [1 ]
Zeng, Yuping [1 ]
Jiang, Dongliang [1 ]
机构：
[1] Chinese Acad Sci, Shanghai Inst Ceram, Shanghai 200050, Peoples R China
来源：
PROGRESSES IN FRACTURE AND STRENGTH OF MATERIALS AND STRUCTURES, 1-4 | 2007年 / 353-358卷
关键词：
Si3N4; SiO2; porous ceramics; microstructure; strength;
D O I：
10.4028/www.scientific.net/KEM.353-358.503
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
An oxidation bonding process was developed to fabricate oxidation-bonded porous silicon nitride (Si3N4) ceramics from alpha-Si3N4 powder in air at 1100-1400 degrees C. Si3N4 particles are bonded by the oxidation-derived silica (SiO2) and the pores derive from the stack of Si3N4 particles and the release of N-2 and SiO gas during the sintering. The microstructure of oxidation-bonded porous Si3N4 ceramics was observed. Moreover, the fracture mechanism was analyzed. Effects of the bonding phases and pores on the flexural strength were investigated. Oxidation-bonded porous Si3N4 ceramics with high flexural strength was obtained by restraining the crystallization of amorphous silica and forming the well-developed necks between Si3N4 particles.
引用
收藏
页码：503 / 506
页数：4
相关论文
共 50 条
  • [31] Preparation of porous silicon nitride ceramics by freeze drying
    Xiao Chun-fang
    Han Bing
    JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2019, 8 (06): : 6202 - 6208
  • [32] Microwave dielectric property of porous silicon nitride ceramics
    Li, Junqi
    Luo, Fa
    Zhu, Dongmei
    Zhou, Wancheng
    HIGH-PERFORMANCE CERAMICS IV, PTS 1-3, 2007, 336-338 : 307 - +
  • [33] Synthesis of Porous Silicon Nitride Ceramics from Diatomite
    Lu, Yuan
    Yang, Jianfeng
    Lu, Weizhong
    Liu, Rongzhen
    Qiao, Guanjun
    Bao, Chonggao
    MATERIALS AND MANUFACTURING PROCESSES, 2010, 25 (09) : 998 - 1000
  • [34] A method for improving the porosity of porous silicon nitride ceramics
    Xu, Zhenru
    Zhang, Nianlin
    Li, Tongyang
    Jiang, Fengchun
    Yu, Yuan
    Wang, Lujie
    Tang, Huaguo
    Qiao, Zhuhui
    JOURNAL OF SOLID STATE CHEMISTRY, 2025, 342
  • [35] Effect of dewaxing procedures of cold isostatically pressed silicon nitride ceramics on its microstructure and fracture strength
    Hotta, T
    Abe, H
    Fukui, T
    Naito, M
    Shinohara, N
    Uematsu, K
    ADVANCED POWDER TECHNOLOGY, 2003, 14 (05) : 505 - 517
  • [36] Characterization of porous silicon nitride ceramics using bentonite as binder and sintering additive
    Jiang, Guang-Peng
    Yang, Jian-Feng
    Gao, Ji-Qiang
    Niihara, Koichi
    MATERIALS CHARACTERIZATION, 2009, 60 (05) : 456 - 460
  • [37] Effect of oxidation on the compressive strength of sintered SiC-fiber bonded ceramics
    Ramirez-Rico, Joaquin
    Martinez-Fernandez, Julian
    Singh, Mrityunjay
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2012, 534 : 394 - 399
  • [38] Microstructure and properties of porous silicon carbide ceramics fabricated by carbothermal reduction and subsequent sintering process
    Eom, Jung-Hye
    Kim, Young-Wook
    Song, In-Hyuck
    Kim, Hai-Doo
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2007, 464 (1-2): : 129 - 134
  • [39] The effect of tape casting parameters on the properties of textured porous silicon nitride ceramics
    Hu, Yiyang
    Xia, Yongfeng
    Zhu, Ming
    Zhao, Jun
    Yao, Dongxu
    Zeng, Yu-Ping
    INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY, 2025, 22 (02)
  • [40] Fabrication of porous silicon carbide ceramics with high porosity and high strength
    Chen, Weiwu
    Miyamoto, Yoshinari
    JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2014, 34 (03) : 837 - 840
12345