Impact of the Allowed Compositional Range of Additively Manufactured 316L Stainless Steel on Processability and Material Properties

被引:7
作者
Grosswendt, Felix [1 ]
Becker, Louis [1 ]
Rottger, Arne [2 ]
Chehreh, Abootorab Baqerzadeh [3 ]
Strauch, Anna Luise [4 ]
Uhlenwinkel, Volker [4 ]
Lentz, Jonathan [1 ]
Walther, Frank [3 ]
Fechte-Heinen, Rainer [4 ,5 ]
Weber, Sebastian [1 ]
Theisen, Werner [1 ]
机构
[1] Ruhr Univ Bochum, Chair Mat Technol, D-44801 Bochum, Germany
[2] Univ Wuppertal, Chair New Mfg Technol & Mat, D-42651 Solingen, Germany
[3] Tech Univ Dortmund, Dept Mat Test Engn, D-44227 Dortmund, Germany
[4] Leibniz Inst Mat Engn IWT, D-28359 Bremen, Germany
[5] Univ Bremen, MAPEX Ctr Mat & Proc, D-28359 Bremen, Germany
关键词
additive manufacturing; powder bed fusion-laser beam; metal (PBF-LB; M); stainless steel (316L); microstructure; solid-state cracking; HIGH-TEMPERATURE BEHAVIOR; BASE WELD METAL; HIGH-STRENGTH; LASER; MICROSTRUCTURE; SOLIDIFICATION; REFINEMENT; DUCTILITY;
D O I
10.3390/ma14154074
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
This work aims to show the impact of the allowed chemical composition range of AISI 316L stainless steel on its processability in additive manufacturing and on the resulting part properties. ASTM A276 allows the chromium and nickel contents in 316L stainless steel to be set between 16 and 18 mass%, respectively, 10 and 14 mass%. Nevertheless, the allowed compositional range impacts the microstructure formation in additive manufacturing and thus the properties of the manufactured components. Therefore, this influence is analyzed using three different starting powders. Two starting powders are laboratory alloys, one containing the maximum allowed chromium content and the other one containing the maximum nickel content. The third material is a commercial powder with the chemical composition set in the middle ground of the allowed compositional range. The materials were processed by laser-based powder bed fusion (PBF-LB/M). The powder characteristics, the microstructure and defect formation, the corrosion resistance, and the mechanical properties were investigated as a function of the chemical composition of the powders used. As a main result, solid-state cracking could be observed in samples additively manufactured from the starting powder containing the maximum nickel content. This is related to a fully austenitic solidification, which occurs because of the low chromium to nickel equivalent ratio. These cracks reduce the corrosion resistance as well as the elongation at fracture of the additively manufactured material that possesses a low chromium to nickel equivalent ratio of 1.0. A limitation of the nickel equivalent of the 316L type steel is suggested for PBF-LB/M production. Based on the knowledge obtained, a more detailed specification of the chemical composition of the type 316L stainless steel is recommended so that this steel can be PBF-LB/M processed to defect-free components with the desired mechanical and chemical properties.
引用
收藏
页数:19
相关论文
共 56 条
  • [31] X-ray diffraction characterization of heavily deformed metallic specimens
    Lutterotti, L
    Gialanella, S
    [J]. ACTA MATERIALIA, 1998, 46 (01) : 101 - 110
  • [32] Residual stresses in selective laser sintering and selective laser melting
    Mercelis, Peter
    Kruth, Jean-Pierre
    [J]. RAPID PROTOTYPING JOURNAL, 2006, 12 (05) : 254 - 265
  • [33] A study of the influence of nitric acid concentration on the corrosion resistance of sintered austenitic stainless steel
    Otero, E
    Pardo, A
    Saenz, E
    Utrilla, MV
    Hierro, P
    [J]. CORROSION SCIENCE, 1996, 38 (09) : 1485 - 1493
  • [34] Selective Laser Melting of Duplex Stainless Steel 2205: Effect of Post-Processing Heat Treatment on Microstructure, Mechanical Properties, and Corrosion Resistance
    Papula, Suvi
    Song, Mingshi
    Pateras, Aaron
    Chen, Xiao-Bo
    Brandt, Milan
    Easton, Mark
    Yagodzinskyy, Yuriy
    Virkkunen, Iikka
    Haenninen, Hannu
    [J]. MATERIALS, 2019, 12 (15)
  • [35] Formation of metastable cellular microstructures in selective laser melted alloys
    Prashanth, K. G.
    Eckert, J.
    [J]. JOURNAL OF ALLOYS AND COMPOUNDS, 2017, 707 : 27 - 34
  • [36] High temperature behavior of Ni-base weld metal - Part II - Insight into the mechanism for ductility dip cracking
    Ramirez, AJ
    Lippold, JC
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2004, 380 (1-2): : 245 - 258
  • [37] High temperature behavior of Ni-base weld metal - Part I. Ductility and microstructural characterization
    Ramirez, AJ
    Lippold, JC
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2004, 380 (1-2): : 259 - 271
  • [38] A PROFILE REFINEMENT METHOD FOR NUCLEAR AND MAGNETIC STRUCTURES
    RIETVELD, HM
    [J]. JOURNAL OF APPLIED CRYSTALLOGRAPHY, 1969, 2 : 65 - &
  • [39] Microstructure and mechanical properties of 316L austenitic stainless steel processed by different SLM devices
    Roettger, A.
    Boes, J.
    Theisen, W.
    Thiele, M.
    Esen, C.
    Edelmann, A.
    Hellmann, R.
    [J]. INTERNATIONAL JOURNAL OF ADVANCED MANUFACTURING TECHNOLOGY, 2020, 108 (03) : 769 - 783
  • [40] Controlling crack formation and porosity in laser powder bed fusion: Alloy design and process optimisation
    Sabzi, Hossein Eskandari
    Maeng, Suhyun
    Liang, Xingzhong
    Simonelli, Marco
    Aboulkhair, Nesma T.
    Rivera-Diaz-del-Castillo, Pedro E. J.
    [J]. ADDITIVE MANUFACTURING, 2020, 34