Dry Reforming of Methane Using Ce-modified Ni Supported on 8%PO4 + ZrO2 Catalysts

Dry reforming of methane (DRM) was studied in the light of Ni supported on 8%PO4 + ZrO2 catalysts. Cerium was used to modify the Ni active metal. Different percentage loadings of Ce (1%, 1.5%, 2%, 2.5%, 3%, and 5%) were tested. The wet incipient impregnation method was used for the preparation of all catalysts. The catalysts were activated at 700 degrees C for 1/2 h. The reactions were performed at 800 degrees C using a gas hourly space velocity of 28,000 mL (h.gcat)(-1). X-ray diffraction (XRD), N-2 physisorption, hydrogen temperature programmed reduction (H-2-TPR), temperature programmed oxidation (TPO), temperature programmed desorption (TPD), and thermogravimetric analysis (TGA) were used for characterizing the catalysts. The TGA analysis depicted minor amounts of carbon deposition. The CO2-TPD results showed that Ce enhanced the basicity of the catalysts. The 3% Ce loading possessed the highest surface area, the largest pore volume, and the greatest pore diameter. All the promoted catalysts enhanced the conversions of CH4 and CO2. Among the promoted catalysts tested, the 10Ni + 3%Ce/8%PO4 + ZrO2 catalyst system operated at 1 bar and at 800 degrees C gave the highest conversions of CH4 (95%) and CO2 (96%). The stability profile of Cerium-modified catalysts (10%Ni/8%PO4 + ZrO2) depicted steady CH4 and CO2 conversions during the 7.5 h time on stream.