Improved Oxidation and Hot Corrosion Resistance of 1Cr11Ni2W2MoV Stainless Steel at 650 °C by a Novel Glass-Ceramic Coating

被引：6

作者：

Chen, Ken ^{[1
]}

Lin, Jiewei ^{[1
]}

Li, Wenfang ^{[1
]}

Zhu, Wen ^{[1
]}

Li, Kang ^{[1
]}

Yi, Aihua ^{[1
]}

Hu, Shaodong ^{[1
]}

Chen, Minghui ^{[2
]}

Wang, Fuhui ^{[2
]}

机构：

[1] Dongguan Univ Technol, Sch Mat Sci & Engn, 1 Daxue Rd, Dongguan 523808, Peoples R China

[2] Northeastern Univ, Shenyang Natl Lab Mat Sci, Sch Mat Sci & Engn, Shenyang 110819, Peoples R China

来源：

CRYSTALS | 2021年 / 11卷 / 10期

基金：

中国国家自然科学基金;

关键词：

glass-ceramics coating; martensitic stainless steel; hot corrosion; oxidation; INITIAL OXIDATION; SELF-DIFFUSION; BEHAVIOR; NACL; CRYSTALLIZATION; SUPERALLOY; KINETICS; ALLOY;

D O I：

10.3390/cryst11101213

中图分类号：

O7 [晶体学];

学科分类号：

0702 ; 070205 ; 0703 ; 080501 ;

摘要：

A novel glass-ceramic coating was applied onto the 1Cr11Ni2W2MoV stainless steel. The oxidation and corrosion behaviors of coated and uncoated steels were comparatively investigated in air and in the presence of NaCl + Na2SO4 eutectic deposits at 650 & DEG;C, respectively. Protective scales formed on the surface of stainless steel prevented the severe oxidation of the alloy. Catastrophic hot corrosion occurred on the steel when a salt film was attached, producing loose iron oxide layers and internal corrosion zone. The glass-ceramic coating acted as a barrier that effectively hindered the invasion of corrosive species during the oxidation and hot corrosion tests.

引用

页数：15

共 23 条

[21] Hot corrosion studies of HVOF-sprayed Cr3C2-NiCr coating on 310S stainless steel in an actual environment of a coal fired boiler
Shukla, V. N.
Jayaganthan, R.
Tewari, V. K.
ADVANCES IN MATERIALS AND PROCESSING: CHALLENGES AND OPPORTUNITIES, 2012, 585 : 483 - 487
[22] Improving the hot corrosion resistance of γ/γ' in Fe-Ni superalloy coated with Cr3C2-20NiCr and NiCrAlY using HVOF thermal spray coating
Septianissa, Selly
Prawara, Budi
Basuki, Eddy Agus
Martides, Erie
Riyanto, Edy
INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE, 2022, 17 (12):
[23] Oxidation Resistance HVOF Sprayed Coating 25% (Cr3C2-25(Ni20Cr))+75%NiCrA1Y on Titanium Alloy
Jegadeeswaran, N.
Ramesh, M. R.
Bhat, K. Udaya
INTERNATIONAL CONFERENCE ON ADVANCES IN MANUFACTURING AND MATERIALS ENGINEERING (ICAMME 2014), 2014, 5 : 11 - 20

← 1 2 3 →