Production of Ductile Iron Castings with Different Matrix Structure

被引：0
|
作者：
Bockus, Stasys [1 ]
Zaldarys, Gintautas [1 ]
机构：
[1] Kaunas Univ Technol, Mfg Technol Dept, LT-44025 Kaunas, Lithuania
来源：
MATERIALS SCIENCE-MEDZIAGOTYRA | 2010年 / 16卷 / 04期
关键词：
ductile iron; matrix structure; section size; mechanical properties; microhardness; SPHEROIDAL GRAPHITE; MECHANICAL-PROPERTIES; NODULE COUNT; COOLING RATE; BEHAVIOR; MICROSTRUCTURE; SOLIDIFICATION; TEMPERATURE; PLATES; DAMAGE;
D O I：
暂无
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The relation between the kind of inoculants, the castings size and matrix structure of ductile iron was investigated. Inoculation was performed by using 4 different inoculants. Ductile iron was cast in test bars with diameters from 3 mm to 50 mm. The study of the microstructure showed that the effect of the kind of inoculant on the content of pearlite is significant only for regular specimen sizes. The hardness value was found to decrease with decreasing pearlite content in the matrix structure of ductile iron. The time between spheroidizing treatment and pouring has strong effect on the ductility of ductile iron. Ce-bearing inoculant reduced this effect. Tests were also conducted to investigate the effects of kind of inoculants and the diameter of specimens on the microhardness of pearlite. It was found that the microhardness of pearlite of small size specimens is higher than this one of large size specimens. Ce-bearing inoculant slightly equalizes pearlite contents and its microhardness in various specimens sizes.
引用
收藏
页码：307 / 310
页数：4
相关论文
共 50 条
  • [1] EVALUATION OF PRODUCING TECHNIQUE FACTORS AFFECTING THE MATRIX MICROSTRUCTURE OF AS-CAST DUCTILE IRON CASTINGS
    Bockus, S.
    Zaldarys, G.
    METALURGIJA, 2011, 50 (01): : 9 - 12
  • [2] Fatigue Characterization and Optimization of the Production Process of Heavy Section Ductile Iron Castings
    Foglio, E.
    Gelfi, M.
    Pola, A.
    Goffelli, S.
    Lusuardi, D.
    INTERNATIONAL JOURNAL OF METALCASTING, 2017, 11 (01) : 33 - 43
  • [3] Effects of Titanium, Cerium or Aluminum Addition on Microstructure and Mechanical Properties of Ductile Iron Castings
    Xu, Mingzhi
    Qing, Jingjing
    Fowler, Shelton
    INTERNATIONAL JOURNAL OF METALCASTING, 2024, 18 (03) : 2003 - 2015
  • [4] Multiphase matrix structure of unalloyed austempered ductile iron
    Yang, Chen
    Cui, Xixi
    Liu, Cheng
    MATERIALS SCIENCE AND TECHNOLOGY, 2018, 34 (03) : 261 - 267
  • [5] Fatigue propagation of long cracks in ferritic thin wall ductile iron castings
    Caldera, M.
    Chapetti, M.
    Massone, J. M.
    Sikora, J. A.
    MATERIALS SCIENCE AND TECHNOLOGY, 2010, 26 (09) : 1102 - 1107
  • [6] Relation between section thickness, microstructure and mechanical properties of ductile iron castings
    Bockus, Stasys
    Venckunas, Arvydas
    Zaldarys, Gintautas
    MATERIALS SCIENCE-MEDZIAGOTYRA, 2008, 14 (02): : 115 - 118
  • [7] Effect of Orientation, Thickness, and Composition on Properties of Ductile Iron Castings
    Shinde, Vasudev D.
    Ravi, B.
    Narasimhan, K.
    MATERIALS AND MANUFACTURING PROCESSES, 2013, 28 (05) : 539 - 544
  • [8] Effect of Inoculants on the Structure and Properties of Thin-Walled Ductile Iron Castings
    Roucka, J.
    Kana, V.
    Krystufek, T. .
    Chylkova, A.
    ARCHIVES OF FOUNDRY ENGINEERING, 2022, 22 (04) : 90 - 95
  • [9] Development of as-cast dual matrix structure (DMS) ductile iron
    Murcia, S. C.
    Paniagua, M. A.
    Ossa, E. A.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2013, 566 : 8 - 15
  • [10] Influence of the Inoculation on the Microstructure of Ductile Iron Castings
    Bockus, S.
    Zaldarys, G.
    MECHANIKA 2009 - PROCEEDINGS OF THE 14TH INTERNATIONAL CONFERENCE, 2009, : 52 - 56
12345