Effects of liquid accelerators on carbonation properties of C3A and C3S hydration products

被引：8

作者：

He, Tingshu ^{[1
]}

Yang, Renhe ^{[1
]}

Guo, Xinqi ^{[2
]}

Xu, Rongsheng ^{[1
]}

Da, Yongqi ^{[1
]}

Fan, Xuna ^{[3
]}

机构：

[1] Xian Univ Architecture & Technol, Coll Mat Sci & Engn, Xian, Shaanxi, Peoples R China

[2] Xiamen Acad Bldg Res Grp Co Ltd, Xiamen, Fujian, Peoples R China

[3] Gansu Ding Li New Mat Co Ltd, Lanzhou, Gansu, Peoples R China

来源：

ADVANCES IN CEMENT RESEARCH | 2021年 / 33卷 / 08期

关键词：

C3A; C3S; ettringite; ALKALINE SHOTCRETE ACCELERATORS; CEMENT SYSTEMS; DURABILITY; STRENGTH; SUPERPLASTICIZERS; PERMEABILITY; SURFACE; PASTE;

D O I：

10.1680/jadcr.19.00135

中图分类号：

TU [建筑科学];

学科分类号：

0813 ;

摘要：

Different liquid accelerators including sodium aluminate liquid accelerator (SAa), fluoaluminate liquid accelerator (Fa) and aluminium sulfate liquid accelerator (ASa) were selected to investigate their influences on the carbonation properties and morphology of tricalcium aluminate (C(3)A) and tricalcium silicate (C3S) hydration products. After an accelerated carbonation test, the relative contents of ettringite (AFt), calcium hydroxide (CH) and calcium carbonate (CaCO3) in the hydration products of C(3)A and C3S samples were analysed by thermogravimetric analysis. The results indicated that the hydration products of C(3)A and C3S with liquid accelerators were easier to carbonate, and the promotion effect of SAa was the most obvious. The morphology of hydrated products of C(3)A and C3S was observed by scanning electron microscopy analysis. It was observed that different liquid accelerators had a different influence on the morphology of C(3)A and C3S hydration products. Among them, ASa had the greatest influence on the morphology of C(3)A and C3S hydration products, and experiments proved that ASa could promote the transformation of AFt into AFm and make the CH crystal structure become thicker and larger.

引用

页码：367 / 376

页数：10

共 50 条

[1] Effects of superplasticizers on the carbonation resistance of C3S and C3A hydration products
He, Tingshu
Shi, Chen
Li, Guoxin
Song, Xuefeng
CONSTRUCTION AND BUILDING MATERIALS, 2012, 36 : 954 - 959
[2] Physicochemical effects of nanosilica on C3A/C3S hydration
Hou, Pengkun
Wang, Xinming
Zhao, Piqi
Wang, Kejin
Kawashima, Shiho
Li, Qinfei
Xie, Ning
Cheng, Xin
Shah, Surendra P.
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2020, 103 (11) : 6505 - 6518
[3] Effect of C3S on the early hydration of C3A
J Therm Anal, 6 (1349):
[4] INVESTIGATION OF THE EFFECTS OF DIETHYLENE GLYCOL ON THE HYDRATION OF C3S AND C3A PASTES
JAKUBEKOVA, D
STIBRANY, P
FRTALOVA, D
JOURNAL OF THERMAL ANALYSIS AND CALORIMETRY, 1988, 33 (03) : 651 - 659
[5] Hydration products of C3A, C3S and Portland cement in the presence of CaCO3
Kakali, G
Tsivilis, S
Aggeli, E
Bati, M
CEMENT AND CONCRETE RESEARCH, 2000, 30 (07) : 1073 - 1077
[6] Investigation of the effects of diethylene glycol on the hydration of C3S and C3A pastes
Jakubekova, D.
Stibrany, P.
Frtalova, D.
Journal of thermal analysis, 1988, 33 (03): : 651 - 659
[7] Effect of temperature and superplasticizer on hydration of C3S and carbonation products of C-S-H
Hu, Xiaochuan
Xu, Lei
Li, Molan
Wang, Junjie
Ran, Bo
Huang, Rong
Zhou, Xiangming
Xiong, Yuzhang
CONSTRUCTION AND BUILDING MATERIALS, 2024, 444
[8] The influence of methylcellulose on the hydration process of C3S, C3A and mixture of these phases
Pichniarczyk, Pawel
7TH SCIENTIFIC-TECHNICAL CONFERENCE ON MATERIAL PROBLEMS IN CIVIL ENGINEERING (MATBUD'2015), 2015, 108 : 220 - 230
[9] The influence of sulfate addition on hydration kinetics and C-S-H morphology of C3S and C3S/C3A systems
Zunino, Franco
Scrivener, Karen
CEMENT AND CONCRETE RESEARCH, 2022, 160
[10] The influence of sulfate addition on hydration kinetics and C-S-H morphology of C3S and C3S/C3A systems
Zunino, Franco
Scrivener, Karen
Cement and Concrete Research, 2022, 160

← 1 2 3 4 5 →