Specimen size effects on gigacycle fatigue properties of high-strength steel under ultrasonic fatigue testing

被引：109
|
作者：
Furuya, Y. [1 ]
机构：
[1] Natl Inst Mat Sci, Tsukuba, Ibaraki 3050047, Japan
来源：
SCRIPTA MATERIALIA | 2008年 / 58卷 / 11期
关键词：
fatigue; gigacycle fatigue; ultrasonic fatigue testing; high-strength steel; size effect;
D O I：
10.1016/j.scriptamat.2008.01.039
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
Ultrasonic fatigue testing was conducted for high-strength steel, employing enlarged specimens with a straight section. The results showed good agreement with conventional servohydraulic fatigue test results, demonstrating the validity of ultrasonic fatigue testing using these enlarged specimens under conditions where fish-eye fractures occur. When the results were compared with those using conventional specimens, specimen size effects were clearly observed: enlarged specimens showed lower fatigue strength due to appearance of larger inclusions in the fish-eye fracture origin. (c) 2008 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
引用
收藏
页码：1014 / 1017
页数：4
相关论文
共 50 条
  • [41] Notch Sensitivity of the Fatigue Limit in High-Strength Steel
    Hamano, Yasuaki
    Koyama, Motomichi
    Hamada, Shigeru
    Noguchi, Hiroshi
    ISIJ INTERNATIONAL, 2016, 56 (08) : 1480 - 1486
  • [42] Gigacycle Fatigue Behavior of High Strength Aluminum Alloys
    Wang, Q. Y.
    Li, T.
    Zeng, X. G.
    FATIGUE 2010, 2010, 2 (01): : 65 - 70
  • [43] FATIGUE CRACK INITIATION AND FATIGUE LIFE TESTING OF HIGH-STRENGTH AUSTENITIC STAINLESS STEEL TUBING WITH INTERNAL HYDROGEN
    San Marchi, Chris
    Ronevich, Joseph A.
    Pohl, Johan
    Ramseyer, Severin
    Cortinovis, Davide
    Eckmann, Stefan
    PROCEEDINGS OF ASME 2023 PRESSURE VESSELS & PIPING CONFERENCE, PVP2023, VOL 5, 2023,
  • [44] Very high cycle fatigue properties of high-strength spring steel 60SiCrV7
    Hui, W. J.
    Zhou, C.
    Zhang, Y. J.
    Zhao, X. L.
    Dong, H.
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2016, 39 (09) : 1081 - 1091
  • [45] Effect of Stress Ratio on Fatigue Properties of High-strength Steels
    Furuya, Yoshiyuki
    Abe, Takayuki
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 2009, 95 (04): : 378 - 383
  • [46] EVALUATION OF ULTRASONIC FATIGUE TESTING PROCESS OF HIGH STRENGTH STEEL BY NON-LINEAR ULTRASONIC ANALYSIS
    Shiwa, M.
    Furuya, Y.
    Yamawaki, H.
    Ito, K.
    Enoki, M.
    REVIEW OF PROGRESS IN QUANTITATIVE NONDESTRUCTIVE EVALUATION, VOLS 28A AND 28B, 2009, 1096 : 1450 - +
  • [47] Nanoprecipitates assisting subsurface cracking in high-strength steel under very high cycle fatigue
    Chen, Yao
    Wang, Shijian
    Li, Haizhou
    Liu, Yongjie
    He, Chao
    Cui, Jie
    Jiang, Qing
    Liu, Chang
    He, Qiyuan
    Liang, Quanwei
    Li, Lang
    Wang, Qingyuan
    SCRIPTA MATERIALIA, 2023, 224
  • [48] Ultrasonic fatigue testing under multiaxial loading on a railway steel
    da Costa, Pedro R.
    Soares, Henrique
    Reis, Luis
    Freitas, Manuel
    INTERNATIONAL JOURNAL OF FATIGUE, 2020, 136
  • [49] Anisotropy effects on gigacycle fatigue behaviour of high Cr alloyed cold work tool steel
    Sohar, Ch. R.
    Betzwar-Kotas, A.
    Gierl, Ch.
    Weiss, B.
    Danninger, H.
    KOVOVE MATERIALY-METALLIC MATERIALS, 2008, 46 (04): : 197 - 207
  • [50] Very High Cycle Fatigue of Butt-Welded High-Strength Steel Plate
    Yeom, Hyunho
    Choi, Byungjoo
    Seol, Taeho
    Lee, Moongu
    Jeon, Yongho
    METALS, 2017, 7 (03)
12345