Effect of minor elements on the creep resistance of Mg-Zn-Mn-(Ca) alloy

Along with alumium, titanium and composite alloys, magnesium alloys have been given much attention by industry for applications such as lightweight automobiles and electronics because of their high strength, low specific density and good damping characteristics. In this paper, creep tests were done with magnesium alloys (Mg-3% Zn-1% Mn, Mg-1.2% Zn-1% Mn, and Mg-3% Zn-1% Mn-0.3% Ca) containing different amounts of Zn to investigate the effect of Zn and Ca on the deformation behavior and the rupture time for Mg alloy creep under elevated temperatures. The alloys were obtained as follows: (1) pure magnesium (9.7 kg) was melted at 720A degrees C in an SF6 atmosphere; (2) the temperature was increased up to 800-820A degrees C after adding 0.3 kg of pure Mn to make the Mg-1% Mn master alloy; (3) the minor element (Zn, Ca) was added to the master alloy; and (4) the magnesium alloy melts were cast into a metallic mold preheated to 150A degrees C. The creep tests were executed under a constant load and temperature to measure the steady-state rate and rupture time of creep. Based on the experimental results, the creep behavior of the alloys seemed to be controlled by dislocation climb at around 0.5 similar to 0.55T(m) (T(m); melting temperature). In addition, the results showed that the addition of Ca was effective for increasing the creep resistance of a Mg alloy: the more Zn present in the alloy, the stronger the creep strength of the alloy.