Tribological properties of plasma sprayed Al/Al2O3 composite coatings

被引：56

作者：

Yin, Zhijian

Tao, Shunyan ^{[1
]}

Zhou, Xiaming

Ding, Chuanxian

机构：

[1] Chinese Acad Sci, Shanghai Inst Ceram, Shanghai 200050, Peoples R China

[2] Chinese Acad Sci, Grad Sch, Beijing 100049, Peoples R China

来源：

WEAR | 2007年 / 263卷

关键词：

Al/Al2O3; composite coating; plasma spraying; friction and wear;

D O I：

10.1016/j.wear.2007.01.052

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

Al2O3 and Al/Al2O3 composite coatings were prepared by atmospheric plasma spraying. The wear and friction properties of both coatings were evaluated under different degrees of severity using a block-on-ring arrangement. It was found that the wear resistance of the Al/Al2O3 composite coating was superior to that of the Al2O3 coating. The improvement in wear resistance of the Al/Al2O3 composite coating was attributed to its higher fracture toughness and adhesion strength as well as better thermal diffusivity. As for the Al/Al2O3 composite coating, the mechanism was mainly adhesion with micro-abrasion and fatigued-induced brittle fracture within splats, and the delamination along splat boundaries only occurred at high load. However, the failure of the Al2O3 coating was predominantly detachment of transferred film and brittle fracture within the splats and delamination along splat boundaries, which were enhanced with the increasing load. (c) 2007 Elsevier B.V. All rialits reserved.

引用

页码：1430 / 1437

页数：8

共 28 条

[1] FRICTION AND WEAR OF CERAMICS [J].