Morphology and composition changes of spinel (MgAl2O4) inclusions in steel

被引：10

作者：

Dogan, N. ^{[1
]}

Longbottom, R. J. ^{[1
]}

Reid, M. H. ^{[1
]}

Chapman, M. W. ^{[2
]}

Wilson, P. ^{[2
]}

Moore, L. ^{[2
]}

Monaghan, B. J. ^{[1
]}

机构：

[1] Univ Wollongong, PYROmet Res Grp, Wollongong, NSW 2522, Australia

[2] BlueScope Steel Ltd, Port Kembla, NSW 2505, Australia

来源：

IRONMAKING & STEELMAKING | 2015年 / 42卷 / 03期

基金：

澳大利亚研究理事会;

关键词：

Inclusion modification; Inclusion reactivity; Spinel; MINIMIZATION; MECHANISM;

D O I：

10.1179/1743281214Y.0000000219

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

In this study, spinel inclusions of close to stoichiometric MgO.Al2O3 composition and known size distribution were added to a liquid steel bath before assessing their reactivity. The inclusions were then tracked for changes in size, morphology and composition with time in an aluminium killed steel at 1600 degrees C, by sampling of the melt followed by automatic SEM based inclusion analysis techniques. The majority of the inclusions in the melt were alumina and complex sulphide inclusions, with the added spinel inclusions being a small proportion of the total inclusions. The proportion of alumina inclusions increased with time. The spinel inclusions were found to be evenly distributed through the melt and there was little change in their average size during the reaction. However, the composition of the inclusions did change, with the Mg/Al mass-% ratio changing from similar to 0.5 to 0.08.

引用

页码：185 / 193

页数：9

共 50 条

[1] Defect processes in MgAl2O4 spinel [J].

Ball, J. A. ;

Murphy, S. T. ;

Grimes, R. W. ;

Bacorisen, D. ;

Smith, R. ;

Uberuaga, B. P. ;

Sickafus, K. E. .

SOLID STATE SCIENCES, 2008, 10 (06) :717-724

[2] Cathodoluminescence analysis for rapid identification of alumina and MgAl2O4 spinel inclusions in steels [J].

Imashuku, Susumu ;

Ono, Koichiro ;

Shishido, Rie ;

Suzuki, Shigeru ;

Wagatsuma, Kazuaki .

MATERIALS CHARACTERIZATION, 2017, 131 :210-216

[3] Synthesis of MgAl2O4 Spinel in a Thermal Plasma [J].

Shekhovtsov, V. V. ;

Skripnikova, N. K. ;

Ulmasov, A. B. .

INORGANIC MATERIALS, 2023, 59 (08) :851-857

[4] Dipole defects in MgAl2O4 spinel crystals [J].

Ayres, F ;

De Souza, SS ;

Blak, AR .

RADIATION EFFECTS AND DEFECTS IN SOLIDS, 2001, 156 (1-4) :305-309

[5] Development of Transparent MgAl2O4 Spinel Ceramics [J].

Li, Fa-hui ;

Li, Jian-Bao ;

Lin, Hong ;

Huang, Cun-Xin ;

Lei, Mu-Yun ;

Du, Hong-Bing .

HIGH-PERFORMANCE CERAMICS VI, 2010, 434-435 :649-+

[6] Non-stoichiometry in MgAl2O4 spinel [J].

Murphy, S. T. ;

Gilbert, C. A. ;

Smith, R. ;

Mitchell, T. E. ;

Grimes, R. W. .

PHILOSOPHICAL MAGAZINE, 2010, 90 (10) :1297-1305

[7] Morphological and Structural Characterization of MgAl2O4 Spinel [J].

Obradovic, Nina ;

Filipovic, Suzana ;

Fahrenholtz, William G. ;

Markinkovic, Bojan A. ;

Rogan, Jelena ;

Levic, Steva ;

Dordevic, Antonije ;

Parolovic, Vladimir B. .

SCIENCE OF SINTERING, 2023, 55 (01) :1-10

[8] Synthesis of MgAl2O4 Spinel in a Thermal Plasma [J].

V. V. Shekhovtsov ;

N. K. Skripnikova ;

A. B. Ulmasov .

Inorganic Materials, 2023, 59 :851-857

[9] Low temperature synthesis of spinel (MgAl2O4) [J].

Singh, VK ;

Sinha, RK .

MATERIALS LETTERS, 1997, 31 (3-6) :281-285

[10] Restraining deactivation of ?-zeolite by modifying with MgAl2O4 spinel in [J].

de Oliveira, Amanda Sayure Kasuya ;

Lopes, Antonio Marcelo Silva ;

Barbosa, Felipe Fernandes ;

da Silva, Francisco Ivan ;

de Sousa, Jose Antonio ;

Pontes, Luiz Antonio Magalhaes ;

Pergher, Sibele B. C. ;

Braga, Tiago Pinheiro .

MOLECULAR CATALYSIS, 2022, 527

← 1 2 3 4 5 →