Investigation of erosive wear behaviors of AA6082-T6 aluminum alloy

被引：15

作者：

Erdogan, Aygen A. ^{[1
]}

Feyzullahoglu, Erol ^{[2
]}

Fidan, Sinan ^{[3
]}

Sinmazcelik, Tamer ^{[2
]}

机构：

[1] Ford Otosan, Dept Prod Dev, Golcuk Kocaeli, Turkey

[2] Kocaeli Univ, Dept Mech Engn, Kocaeli, Turkey

[3] Kocaeli Univ, Fac Aeronaut & Astronaut, Kocaeli, Turkey

来源：

PROCEEDINGS OF THE INSTITUTION OF MECHANICAL ENGINEERS PART L-JOURNAL OF MATERIALS-DESIGN AND APPLICATIONS | 2020年 / 234卷 / 03期

关键词：

6082 Aluminum alloy; solid particle erosion; surface morphology; roughness; SOLID-PARTICLE EROSION; LAYERS; SIZE;

D O I：

10.1177/1464420719899686

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

AA6082-T6 aluminum alloys are widely used in various applications in automotive and aircraft industries. They offer an attractive combination of surface properties, strength and corrosion resistance. The structural components manufactured by AA6082-T6 aluminum alloys can be exposed to impingement of solid particles throughout their service life. In this study, erosive wear behaviors of AA6082-T6 aluminum alloy were investigated. For the evaluation of erosive wear induced by solid particle impacts, a detailed study was conducted on AA6082-T6 aluminum alloy by using aluminum oxide (Al2O3) erodent particles. Two different particles were used in solid particle erosion tests, which are 60 mesh (212-300 mu m) and 120 mesh (90-125 mu m), respectively. Also, the aluminum alloy samples were tested under two different air pressures (1.5 bar and 3 bar). The erosive wear tests were carried out according to ASTM G76 standard at six various impact angles (15 degrees, 30 degrees, 45 degrees, 60 degrees, 75 degrees, 90 degrees). The surface roughness and morphology of worn samples were analyzed by using a non-contact laser profilometer. It was found that erodent particle size affected the surface erosion damage, erosion rate, crater morphology and roughness. The eroded surfaces of specimens were analyzed by SEM. The surfaces of specimens were also investigated by using EDS in SEM studies.

引用

页码：520 / 530

页数：11

共 20 条

[11]

Levy AV, 1995, SOLID PARTICLE EROSI, P11

[12]

Li D, 2019, FAST HIGH RESOLUTION

[13] A numerical study on the effect of particle shape on the erosion of ductile materials [J].

Liu, Z. G. ;

Wan, S. ;

Nguyen, V. B. ;

Zhang, Y. W. .

WEAR, 2014, 313 (1-2) :135-142

[14] Solid-particle erosion and protective layers for steam turbine blading [J].

Mann, BS .

WEAR, 1999, 224 (01) :8-12

[15] Influence of alumina dispersoid and test parameters on erosive wear behaviour of a cast zinc-aluminium alloy [J].

Modi, OP ;

Prasad, BK ;

Jha, AK .

WEAR, 2006, 260 (7-8) :895-902

[16] MEASUREMENT OF SOLID PARTICLE VELOCITY IN EROSIVE WEAR [J].

RUFF, AW ;

IVES, LK .

WEAR, 1975, 35 (01) :195-199

[17]

Stachowiak GW, 2013, ENG TRIBOLOGY, P501

[18] Erosion tipple formation mechanism in aluminum and aluminum alloys [J].

Talia, JE ;

Ballout, YA ;

Scattergood, RO .

WEAR, 1996, 196 (1-2) :285-294

[19] Erosive wear of plasma electrolytic oxidation layers on aluminium alloy 6061 [J].

Trevino, M. ;

Mercado-Solis, R. D. ;

Colas, R. ;

Perez, A. ;

Talamantes, J. ;

Velasco, A. .

WEAR, 2013, 301 (1-2) :434-441

[20]

Yildiran Y, 2014, ACTA PHYS POL A, V125, P523

← 1 2 →