A comparison of the electrochemical behaviour of W-M-N (M=Ni, Ti, Al) thin film coatings on high speed steel

被引：17

作者：

Brett, CMA ^{[1
]}

Cavaleiro, A

机构：

[1] Univ Coimbra, Dept Quim, P-3049 Coimbra, Portugal

[2] Univ Coimbra, Dept Engn Mecan, P-3030 Coimbra, Portugal

来源：

THIN SOLID FILMS | 1998年 / 322卷 / 1-2期

关键词：

hard coatings; thin films; tungsten-based coatings; corrosion; high speed steel;

D O I：

10.1016/S0040-6090(97)00916-4

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The electrochemical behaviour of W-M-N (M = Ni, Ti, Al) thin-film hard coatings on high speed steel has been studied. Films of 4 mu m thickness of W-Ni, W-Ti and W-Ti-Al with and without nitrogen were produced by DC diode sputtering. Electrochemical measurements were carried out in aqueous potassium chloride solution. Open circuit potential measurements, Tafel plots and electrochemical impedance all show the importance of the influence of nitrogen on the coating behaviour, and some differences between coating types due to the combination of metallic elements are evident. Corrosion is localised at specific points in the coating, which appear in the first hour after immersion. They exhibit the same general features in all cases, involving corrosion beneath the coating followed by film rupture. Electrochemical observations are supported by scanning electron microscopy observations, X-ray diffraction and microindentation measurements before and after corrosion has taken place. A model describing the corrosion process is developed and discussed. (C) 1998 Elsevier Science S.A. All rights reserved.

引用

页码：263 / 273

页数：11

共 27 条

[1]

AFFOLTER K, 1985, P MAT RES SOC S, V17, P167

[2] ENHANCEMENT OF THE REACTIVE DEPOSITION RATE OF TIN FILMS AT LOW NITROGEN-CONTENT [J].

BARANKOVA, H ;

BARDOS, L ;

BERG, S .

JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1994, 141 (01) :L8-L9

[3] EFFECT OF CONTAMINATION REACTIONS ON THE COMPOSITION AND MECHANICAL-PROPERTIES OF MAGNETRON SPUTTERED TIN COATINGS [J].

BERG, S ;

EGUCHI, N ;

GRAJEWSKI, V ;

KIM, SW ;

FROMM, E .

SURFACE & COATINGS TECHNOLOGY, 1991, 49 (1-3) :336-341

[4]

Brett C. M. A., 1995, Materials Science Forum, V192-194, P797, DOI 10.4028/www.scientific.net/MSF.192-194.797

[5] Corrosion of sputtered W-Ni-N hard coatings in chloride media [J].

Brett, CMA ;

Nimigean, CM .

THIN SOLID FILMS, 1997, 311 (1-2) :1-6

[6] Influence of anions on the corrosion of high speed steel [J].

Brett, CMA ;

Melo, PIC .

JOURNAL OF APPLIED ELECTROCHEMISTRY, 1997, 27 (08) :959-964

[7] EFFECT OF COMPOSITION AND THICKNESS ON CORROSION BEHAVIOR OF TIN AND ZRN THIN-FILMS [J].

BROWN, R ;

ALIAS, MN ;

FONTANA, R .

SURFACE & COATINGS TECHNOLOGY, 1993, 62 (1-3) :467-473

[8] INFLUENCE OF DEPOSITION CONDITIONS ON THE MORPHOLOGY OF SPUTTERED W-C-(CO) FILMS [J].

CAVALEIRO, A ;

VIEIRA, MT ;

LEMPERIERE, G .

THIN SOLID FILMS, 1992, 213 (01) :6-12

[9] THE STRUCTURE OF THIN-FILMS DEPOSITED FROM A SINTERED TUNGSTEN CARBIDE WITH A HIGH COBALT CONTENT (15 WT-PERCENT) [J].

CAVALEIRO, A ;

VIEIRA, MT .

THIN SOLID FILMS, 1990, 185 (02) :199-217

[10] INFLUENCE OF DEPOSITION CONDITIONS ON THE ADHESION OF SPUTTER-DEPOSITED W-C-(CO) FILMS [J].

CAVALEIRO, A ;

VIEIRA, MT .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1991, 140 :631-638

← 1 2 3 →