Passivity behavior of melt-spun Mg-Y alloys

被引:89
作者
Yao, HB [1 ]
Li, Y
Wee, ATS
机构
[1] Natl Univ Singapore, Dept Mat Sci, Singapore 119260, Singapore
[2] Natl Univ Singapore, Dept Phys, Singapore 119260, Singapore
关键词
passivity; native film; passive film; incorporation;
D O I
10.1016/S0013-4686(03)00605-4
中图分类号
O646 [电化学、电解、磁化学];
学科分类号
081704 ;
摘要
Several Mg-Y binary ribbons with Y content up to similar to17.9 at.% were fabricated by melt-spinning. X-ray diffraction (XRD) revealed that the phase structure changes with increasing Y content from extended solid solution to partially amorphous, and then fully intermetallic Mg24Y5. Anodic potentiodynamic polarization performed in 0.01 M NaCl electrolyte (pH = 12) revealed improved anodic passivity behavior compared to pure Mg for all the Mg-Y alloys. X-ray photoelectron spectroscopy (XPS) revealed that the improved passivity of Mg-Y was more related to the elemental oxidation state rather than the concentration of the surface components. To study the effect of Cl- ion on the passivity behavior, anodic potentiodynantic and potentiostatic polarization were performed on Mg-17.9 at.% Y in alkaline (pH = 12) NaCl electrolytes containing Cl- ion in the concentration range from 0.00 to 0.50 M. The passive films formed in 0.01 M NaCl electrolyte were similar to the native film, which were composed of MgO and Y2O3. No CO32- and Cl- ions were incorporated into the passive film. The passivity was significantly degraded in the electrolytes containing higher Cl- concentration (0.1 and 0.5 M). Detailed XPS revealed that the surface films under these conditions were composed of much hydrated species Mg(OH)(2) and YOOH and/or Y(OH)(3) and CO32- was incorporated into the surface film. The incorporation Of Y2O3 in the passive film was given as the reason for the enhanced passivity properties of Mg-Y ribbons. The mechanism of Cl- and CO32- ions to the degradation of the passivity was discussed. (C) 2003 Elsevier Ltd. All rights reserved.
引用
收藏
页码:4197 / 4204
页数:8
相关论文
共 29 条
[1]  
AHMED M, 1992, MAGNESIUM ALLOYS THE, P25
[2]  
[Anonymous], CORROSION LIGHT META
[3]   DEVELOPMENT OF CORROSION-RESISTANT MAGNESIUM ALLOYS .1. CHARACTERIZATION OF SPLAT QUENCHED MG-10AL AND MG-16AL ALLOYS [J].
BALIGA, CB ;
TSAKIROPOULOS, P .
MATERIALS SCIENCE AND TECHNOLOGY, 1993, 9 (06) :507-511
[4]  
Briggs D., 1990, PRACTICAL SURFACE AN, VI, P245
[5]  
DAS SK, 1986, P 43 WORLD MAGN C JU, P1
[6]  
Diplas S., 1998, Materials Science and Technology, V14, P699
[7]  
HEHMANN F, 1989, J MATER SCI, V24, P2369, DOI 10.1007/BF01174498
[8]  
HENNING W, 1985, STRENGTH METALS ALLO, P803
[9]   SUBEUTECTOID DEGRADATION OF YTTRIA-STABILIZED TETRAGONAL ZIRCONIA POLYCRYSTAL AND CERIA-DOPED YTTRIA-STABILIZED TETRAGONAL ZIRCONIA POLYCRYSTAL CERAMICS [J].
HERNANDEZ, MT ;
JURADO, JR ;
DURAN, P ;
FIERRO, JLG .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1991, 74 (06) :1254-1258
[10]   ROLE OF O2-, OH- AND ANION VACANCIES IN THE DEGRADATION OF Y-TZP IN MOIST ENVIRONMENTS [J].
HUGHES, AE ;
CIACCHI, FT ;
BADWAL, SPS .
JOURNAL OF MATERIALS CHEMISTRY, 1994, 4 (02) :257-263