Grain boundary sliding in a superplastic zinc-aluminum alloy processed using severe plastic deformation

被引：53
|
作者：
Kawasaki, Megumi [1 ,2 ]
Langdon, Terence G. [1 ,2 ,3 ]
机构：
[1] Univ So Calif, Dept Aerosp & Mech Engn, Los Angeles, CA 90089 USA
[2] Univ So Calif, Dept Mat Sci, Los Angeles, CA 90089 USA
[3] Univ Southampton, Sch Engn Sci, Mat Res Grp, Southampton SO17 1BJ, Hants, England
来源：
MATERIALS TRANSACTIONS | 2008年 / 49卷 / 01期
关键词：
equal-channel angular pressing; grain boundary sliding; superplasticity; ultrafine grains; zinc-aluminum alloy;
D O I：
10.2320/matertrans.ME200720
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
A Zn-22% Al eutectoid alloy was processed by Equal-Channel Angular Processing (ECAP) to produce a grain size of similar to 0.8 mu m. Tensile testing at 473 K gave a maximum elongation of similar to 2230% at a strain rate of 1.0 x 10(-2) s(-1). The significance of grain boundary sliding was evaluated by taking measurements of offsets in surface marker lines at an elongation of 30%. The highest sliding contribution was recorded under testing conditions corresponding to the maximum superplastic elongation. Detailed measurements showed that relatively large offsets occurred at the Zn-Zn and Zn-Al interfaces but there were smaller offsets at the Al-Al interfaces. It is concluded that grain boundary sliding is the dominant flow process during superplastic deformation.
引用
收藏
页码：84 / 89
页数：6
相关论文
共 50 条
  • [21] Forging studies with severe plastic deformation processed aluminum alloy 6061
    Srinivasan, R
    Chaudhury, P
    THERMEC'2003, PTS 1-5, 2003, 426-4 : 267 - 272
  • [22] PRECISION FORGING OF HIGH-STRENGTH SUPERPLASTIC ZINC-ALUMINUM ALLOY
    BALLIETT, RW
    FORSTER, JA
    DUNCAN, JL
    JOM-JOURNAL OF METALS, 1975, 27 (12): : A54 - A54
  • [23] PRECISION FORGING OF A HIGH-STRENGTH SUPERPLASTIC ZINC-ALUMINUM ALLOY
    BALLIETT, RW
    FORSTER, JA
    DUNCAN, JL
    METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1978, 9 (09): : 1259 - 1264
  • [24] MICROSTRUCTURAL-MECHANISM RELATIONSHIP IN ZINC-ALUMINUM EUTECTOID SUPERPLASTIC ALLOY
    NAZIRI, H
    PEARCE, R
    BROWN, MH
    HALE, KF
    ACTA METALLURGICA, 1975, 23 (04): : 489 - 496
  • [25] The significance of grain boundary sliding in the superplastic Zn-22 % Al alloy processed by ECAP
    Kawasaki, Megumi
    Langdon, Terence G.
    JOURNAL OF MATERIALS SCIENCE, 2013, 48 (13) : 4730 - 4741
  • [26] Influence of grain size fluctuations on ductility of superplastic magnesium alloys processed by severe plastic deformation
    del Valle, J. A.
    Ruano, O. A.
    MATERIALS SCIENCE AND TECHNOLOGY, 2008, 24 (10) : 1238 - 1244
  • [27] EVIDENCE FOR IMPORTANCE OF CRYSTALLOGRAPHIC SLIP DURING SUPERPLASTIC DEFORMATION OF EUTECTIC ZINC-ALUMINUM
    PACKER, CM
    JOHNSON, RH
    SHERBY, OD
    TRANSACTIONS OF THE METALLURGICAL SOCIETY OF AIME, 1968, 242 (12): : 2485 - &
  • [28] Deformation Behavior and Microstructure of 6061 Aluminum Alloy Processed by Severe Plastic Deformation Using Biaxial Alternate Forging
    Ha, Seong-Ho
    Shin, Young-Chul
    MATERIALS, 2024, 17 (05)
  • [29] RATE OF GRAIN BOUNDARY SLIDING DURING SUPERPLASTIC DEFORMATION.
    Kaminskiy, V.M.
    Physics of Metals and Metallography, 1986, 61 (06): : 162 - 164
  • [30] OBSERVATIONS OF GRAIN-BOUNDARY SLIDING DURING SUPERPLASTIC DEFORMATION
    RAI, G
    GRANT, NJ
    METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1983, 14 (07): : 1451 - 1458
12345