Chitosan/PEO nanofibers containing Calendula officinalis extract: Preparation, characterization, in vitro and in vivo evaluation for wound healing applications

Wound healing is a complex pathophysiological process, highlighting the importance of effective and thorough wound care along with the prevention of wound infection, a major barrier that can slow down or even disrupt the healing process. To date, there are plenty of herbal plants well known and historically supernatural, showing profound wound healing effects. Application of such herbal extracts/ingredients in electrospun nanofiber platforms has shown promising outcomes in improving wound healing process. Based on these facts, we loaded Calendula officinalis extract (CO) in chitosan/polyethylene oxide scaffolds (CS/PEO) by electrospinning. Using SEM, morphology of electrospun scaffolds showed a narrow range of fiber diameter, around 143--252 nm, with uniform and bead-free appearance. FT-IR spectroscopy confirmed the presence of CO extract in nanofibrous scaffolds. Of importance, incorporation of CO extract improved mechanical properties of CS/PEO nanofibers. A 1602 cP reduction in viscosity and a 0.892 ms/cm increase in the conductivity of the solution was observed after addition of the CO extract. CO extract showed strong antibacterial properties with 96% and 94% reduction in Gram positive and Gram negative bacteria, respectively. In vitro studies with fibroblast cells confirmed enhanced proliferation, growth and attachment of the cells. The in vivo and histological analysis of rat wounds, revealed excellent wound healing ability of CS/PEO/CO dressings (87.5 % wound closure after 14 days) via improving collagen synthesis, re-epithelization and remodeling of the tissue. In sum, our findings show that CS/PEO/CO scaffolds can be used as a promising dressing for the treatment of skin wounds.