Reduction in secondary dendrite arm spacing in cast aluminium alloy A356 by Sb addition

被引:15
作者
Boontein, S. [2 ]
Srisukhumbovornchai, N. [2 ]
Kajornchaiyakul, J. [3 ]
Limmaneevichitr, C. [1 ]
机构
[1] King Mongkuts Univ Technol Thonburi, Fac Engn, Dept Prod Engn, Bangkok 10140, Thailand
[2] King Mongkuts Univ Technol Thonburi, Sch Energy Environm & Mat, Bangkok 10140, Thailand
[3] Natl Met & Mat Technol Ctr, Pathum Thani 12120, Thailand
关键词
SDAS; Antimony; Al-Si alloy; Directional solidification; UNSTEADY-STATE CONDITIONS; AL-CU ALLOYS; MICROSTRUCTURAL DEVELOPMENT; MECHANICAL-PROPERTIES; SI ALLOYS; SOLIDIFICATION; ANTIMONY;
D O I
10.1179/1743133610Y.0000000007
中图分类号
TF [冶金工业];
学科分类号
0806 ;
摘要
The effects of Sb on the secondary dendrite arm spacing (SDAS) were investigated in directional solidification experiments under different cooling rates. The addition of Sb reduced the average SDAS at higher Sb contents. The most effective reduction occurs at 0.12 wt-%Sb. Our results also reveal a reduced variation in the SDAS upon the addition of Sb in the higher range, i.e. 0.18-0.30 wt-%. We suggest that the reduced variation in the SDAS upon addition of Sb in this range resulted from the interaction between the accumulation of Sb at the solid/liquid interface that increases the instability at the solid/liquid interface and later decreases the SDAS and a high concentration of Sb that increases the accumulation of Sb at the solid/liquid interface and results in a larger amount of AlSb or Mg3Sb2 intermetallic phases and a higher latent heat.
引用
收藏
页码:108 / 112
页数:5
相关论文
共 25 条
[1]   EFFECT OF CE ON THE INTERFACE STABILITY AND DENDRITE ARM SPACING OF AL-CU ALLOYS [J].
AN, GY ;
LIU, LX ;
GU, GD .
JOURNAL OF CRYSTAL GROWTH, 1987, 83 (01) :96-100
[2]   Thermodynamic modeling of the Mg-Al-Sb system [J].
Balakumar, T ;
Medraj, M .
CALPHAD-COMPUTER COUPLING OF PHASE DIAGRAMS AND THERMOCHEMISTRY, 2005, 29 (01) :24-36
[3]  
Boontein S, 2008, J MATER SCI TECHNOL, V24, P25
[4]   Dendrite coarsening during directional solidification of Al-Cu-Mn alloys [J].
Chen, M ;
Kattamis, TZ .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1998, 247 (1-2) :239-247
[5]   Simulation of the columnar-to-equiaxed transition in directionally solidified Al-Cu alloys [J].
Dong, HB ;
Lee, PD .
ACTA MATERIALIA, 2005, 53 (03) :659-668
[6]  
Flemings M.C., 1974, SOLIDIFICATION PROCE, P146
[7]  
Flemings M.C., 1991, T AM FOUNDRYMENS SOC, V99, P501
[8]  
Gruzleski J.E., 1990, TREATMENT LIQUID ALU
[9]   Effect of antimony on the phase equilibrium of binary Al-Si alloys [J].
Hansen, SC ;
Loper, CR .
CALPHAD-COMPUTER COUPLING OF PHASE DIAGRAMS AND THERMOCHEMISTRY, 2000, 24 (03) :339-352
[10]   DENDRITIC GROWTH [J].
HORWATH, JA ;
MONDOLFO, LF .
ACTA METALLURGICA, 1962, 10 (NOV) :1037-&