Effect of cryogenic treatment on microstructure and mechanical behaviors of the Cu-based bulk metallic glass matrix composite

被引:13
作者
Ma, Guozhi [1 ]
Chen, Ding [1 ]
Chen, Zhenhua [1 ]
Li, Wei [1 ]
机构
[1] Hunan Univ, Sch Mat Sci & Engn, Changsha 410082, Hunan, Peoples R China
基金
中国国家自然科学基金;
关键词
Cu-based bulk metallic glass composite; Cryogenic treatment; Martensite; Fracture; FORMING ABILITY; STRENGTH; FRACTURE; ALLOY; DEFORMATION; PLASTICITY; FAILURE; FLOW;
D O I
10.1016/j.jallcom.2010.06.063
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
Effect of cryogenic treatment (CT) on microstructure and mechanical properties of the Cu-based bulk metallic glasses matrix composite (Cu46Zr46Al8) was investigated. CT brought about the refinement of the primary CuZr phase, the formation of the martensite phase accompanying with the morphology modification of the CuZr precipitates, contributing to the improvement in the microhardness and the compression fracture strength. The size of the CuZr crystalline phase was reduced from about 3 mu m to 2 mu m and the morphology of the CuZr precipitate was transformed from the rotundity to the short rod-shape. The compression fracture strength and the microhardness of the as-cast Cu46Zr46Al8 composite were 1340 MPa and 512 Hv respectively, while they were 1759 Mpa and 574 Hv respectively after CT. Furthermore, CT accelerated the fracture morphology transformation from the ductile to the brittle. The possible mechanisms involved in microstructural modification and strength as well as microhardness improvement were discussed. (C) 2010 Published by Elsevier B.V.
引用
收藏
页码:319 / 323
页数:5
相关论文
共 36 条
[1]   New features of the low temperature ductile shear failure observed in bulk amorphous alloys [J].
Bengus, VZ ;
Tabachnikova, ED ;
Miskuf, J ;
Csach, K ;
Ocelík, V ;
Johnson, WL ;
Molokanov, VV .
JOURNAL OF MATERIALS SCIENCE, 2000, 35 (17) :4449-4457
[2]  
Bian Z, 2000, T NONFERR METAL SOC, V10, P345
[3]   Thermal and mechanical properties of Cu-Zr-Al bulk metallic glasses [J].
Cheung, T. L. ;
Shek, C. H. .
JOURNAL OF ALLOYS AND COMPOUNDS, 2007, 434 :71-74
[4]   Effect of relaxation and primary nanocrystallization on the mechanical properties of Cu60Zr22Ti18 bulk metallic glass [J].
Concustell, A ;
Alcalá, G ;
Mato, S ;
Woodcock, TG ;
Gebert, A ;
Eckert, J ;
Baró, MD .
INTERMETALLICS, 2005, 13 (11) :1214-1219
[5]   Basic mechanical behaviors and mechanics of shear banding in BMGs [J].
Dai, L. H. ;
Bai, Y. L. .
INTERNATIONAL JOURNAL OF IMPACT ENGINEERING, 2008, 35 (08) :704-716
[6]   Designing bulk metallic glass and glass matrix composites in martensitic alloys [J].
Das, J. ;
Pauly, S. ;
Bostroem, M. ;
Durst, K. ;
Goeken, M. ;
Eckert, J. .
JOURNAL OF ALLOYS AND COMPOUNDS, 2009, 483 (1-2) :97-101
[7]   Strengthening of multicomponent glass-forniing alloys by microstructure design [J].
Eckert, J. ;
Das, J. ;
Loeser, W. ;
Roy, S. K. ;
Gebert, A. .
JOURNAL OF NON-CRYSTALLINE SOLIDS, 2007, 353 (32-40) :3742-3749
[8]   High strength ductile Cu-base metallic glass [J].
Eckert, J. ;
Das, J. ;
Kim, K. B. ;
Baier, F. ;
Tang, M. B. ;
Wang, W. H. ;
Zhang, Z. F. .
INTERMETALLICS, 2006, 14 (8-9) :876-881
[9]   Mean stress effects on flow localization and failure in a bulk metallic glass [J].
Flores, KM ;
Dauskardt, RH .
ACTA MATERIALIA, 2001, 49 (13) :2527-2537
[10]   Inhomogeneous deformation in metallic glasses [J].
Huang, R ;
Suo, Z ;
Prevost, JH ;
Nix, WD .
JOURNAL OF THE MECHANICS AND PHYSICS OF SOLIDS, 2002, 50 (05) :1011-1027