One-step preparation of TaIr3-based material and its ablation performance under extreme environmental conditions

被引：17

作者：

Baklanova, Natalya I. ^{[1
]}

Lozanov, Victor V. ^{[1
]}

Titov, Anatoly T. ^{[2
]}

机构：

[1] RAS, Inst Solid State Chem & Mechanochem SB, Kutateladze St 18, Novosibirsk 630128, Russia

[2] RAS, VS Sobolev Inst Geol & Mineral SB, Koptyug Ave 3, Novosibirsk 630090, Russia

来源：

CORROSION SCIENCE | 2018年 / 143卷

基金：

俄罗斯科学基金会;

关键词：

Intermetallics; Tantalum oxide; SEM; X-ray diffraction; High temperature corrosion; Oxidation; OXIDATION BEHAVIOR; MECHANICAL-PROPERTIES; PLATINUM; CARBIDES; IRIDIUM; PHASE; MICROSTRUCTURE; INTERMETALLICS; ALLOYS;

D O I：

10.1016/j.corsci.2018.08.044

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The solid-state interaction of TaC with Ir within the 1000-1600 degrees C temperature range leads to the formation of TaIr3 intermetallics. The durability of the TaIr3-based system with a silicon additive was studied under extreme environmental conditions. The TaIr3-based material displays satisfactory ablation resistance at 2000 degrees C in air in arc-jet. The post-test microstructural and XRD analysis of the developed material allowed us to propose the role of different constituents of the Ta - C - Ir - Si system. The iridium-containing phases play the most significant role in favorable ablation behavior of the developed system.

引用

页码：337 / 346

页数：10

共 42 条

[1] CATALYTIC-OXIDATION OF GRAPHITE BY IRIDIUM AND RHODIUM [J].

BAKER, RTK ;

SHERWOOD, RD .

JOURNAL OF CATALYSIS, 1980, 61 (02) :378-389

[2] Microstructure and oxidation behaviour of Ir-rich Ir-Al binary alloys [J].

Bao, Z. B. ;

Murakami, H. ;

Yamabe-Mitarai, Y. .

CORROSION SCIENCE, 2014, 87 :306-311

[3] THE FORMATION OF PATTERNS IN NONEQUILIBRIUM GROWTH [J].

BENJACOB, E ;

GARIK, P .

NATURE, 1990, 343 (6258) :523-530

[4]

Chase M.W, 1998, J. Phys. Chem. Ref. Data, V9, P1, DOI 10.18434/T42S31

[5] A FUNDAMENTAL PARAMETERS APPROACH TO X-RAY LINE-PROFILE FITTING [J].

CHEARY, RW ;

COELHO, A .

JOURNAL OF APPLIED CRYSTALLOGRAPHY, 1992, 25 (pt 2) :109-121

[6]

Chen Z., 1997, APPL SURF SCI, V17, P1325

[7]

Criscione J. M., 1964, MLTDR64173 AIR FOR 2, P156

[8]

Criscione J. M., 1964, NASACR74187 UN CARB, P45

[9] Comparison of the oxidation behaviour of two dense hot isostatically pressed tantalum carbide (TaC and Ta2C) materials [J].

DesmaisonBrut, M ;

Alexandre, N ;

Desmaison, J .

JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 1997, 17 (11) :1325-1334

[10]

FERGUSON WH, 1963, T METALL SOC AIME, V227, P1401

← 1 2 3 4 5 →