An experimental study on the bond strength between reinforcement bars and concrete as a function of concrete cover, strength and corrosion level

被引：220
|
作者：
Yalciner, Hakan [1 ]
Eren, Ozgur [1 ]
Sensoy, Serhan [1 ]
机构：
[1] Eastern Mediterranean Univ, Dept Civil Engn, TR-10 Gazimagusa, Mersin, Turkey
来源：
CEMENT AND CONCRETE RESEARCH | 2012年 / 42卷 / 05期
关键词：
Corrosion; Pullout test; Bond strength; Bond-slip;
D O I：
10.1016/j.cemconres.2012.01.003
中图分类号：
TU [建筑科学];
学科分类号：
0813 ;
摘要：
The effect of corrosion on the bond strength between reinforcement bars and concrete was studied in a series of experiments. An accelerated corrosion method was used to corrode the reinforcement bars embedded in concrete specimens. Pullout tests were performed to develop an empirical model for the ultimate bond strength by evaluating bond strengths in two different concrete mixes, three concrete cover depths and different mass losses of reinforcement bars after corrosion. Bond-slip relationships for the different corrosion levels were compared. It was found that the relationship between bond strength and concrete strength in uncorroded specimens differed from that of corroded specimens set in high-strength concrete because of brittleness in the corroded specimens, which caused a sudden loss of bond strength. The results revealed that specimens with higher concrete strength levels and corroded reinforcements showed a higher percentage of bond strength degradation due to concrete cracking during the pullout tests. (C) 2012 Elsevier Ltd. All rights reserved.
引用
收藏
页码：643 / 655
页数：13
相关论文
共 50 条
  • [31] EFFECT OF PIGMENTS ON BOND STRENGTH BETWEEN COLOURED CONCRETE AND STEEL REINFORCEMENT
    ASSAAD, J. O. S. E. P. H. J.
    MATTA, M. A. T. T. H. E. W.
    SAADE, J. A. D.
    ACTA POLYTECHNICA, 2022, 62 (02) : 248 - 261
  • [32] Evaluation of the impact of corrosion of hot-dip galvanized reinforcement on bond strength with concrete - A review
    Pokorny, Petr
    Tej, Petr
    Kouril, Milan
    CONSTRUCTION AND BUILDING MATERIALS, 2017, 132 : 271 - 289
  • [33] Bond between Steel Reinforcement Bars and Seawater Concrete
    Adnan
    Parung, Herman
    Tjaronge, M. W.
    Djamaluddin, Rudy
    CIVIL ENGINEERING JOURNAL-TEHRAN, 2020, 6 : 61 - 68
  • [34] Evaluation of the bond properties between concrete and reinforcement as a function of the degree of reinforcement corrosion
    Lee, HS
    Noguchi, T
    Tomosawa, F
    CEMENT AND CONCRETE RESEARCH, 2002, 32 (08) : 1313 - 1318
  • [35] Bond strength prediction of steel bars in low strength concrete by using ANN
    Ahmed, Sohaib
    Pilakoutas, Kypros
    Rafi, Muhammad M.
    Zaman, Qaiser U.
    COMPUTERS AND CONCRETE, 2018, 22 (02) : 249 - 259
  • [36] Bond strength of hot-dip galvanized hooked bars in high strength concrete structures
    Hamad, Bilal S.
    Jumaa, Ghaida K.
    CONSTRUCTION AND BUILDING MATERIALS, 2008, 22 (10) : 2042 - 2052
  • [37] Experimental investigations on bond strength between coconut fibre and concrete
    Ali, Majid
    Li, Xiaoyang
    Chouw, Nawawi
    MATERIALS & DESIGN, 2013, 44 : 596 - 605
  • [38] EFFECTS OF CRACK WIDTHS AND ENVIRONMENTS ON THE BOND STRENGTH BETWEEN CONCRETE AND STEEL BARS
    Faye, Papa
    Shen, Bei
    Ye, Yinghua
    Diao, Bo
    FUNDAMENTAL RESEARCH IN STRUCTURAL ENGINEERING: RETROSPECTIVE AND PROSPECTIVE, VOLS 1 AND 2, 2016, : 1570 - 1575
  • [39] Bond strength of hot-dip galvanized hooked bars in normal strength concrete structures
    Hamad, Bilal S.
    Jumaa, Ghaida' K.
    CONSTRUCTION AND BUILDING MATERIALS, 2008, 22 (06) : 1166 - 1177
  • [40] Residual bond strength between steel bars and concrete after elevated temperatures
    Bingol, A. Ferhat
    Gul, Ruestem
    FIRE SAFETY JOURNAL, 2009, 44 (06) : 854 - 859
12345