Fatigue of stress corrosion cracks in X65 pipeline steels

被引：31
|
作者：
Gamboa, E. [1 ]
Linton, V. [1 ]
Law, M. [2 ]
机构：
[1] Univ Adelaide, Sch Mech Engn, Adelaide, SA 5005, Australia
[2] Australian Nucl Sci & Technol Org, PMBI, Menai, NSW 2234, Australia
来源：
INTERNATIONAL JOURNAL OF FATIGUE | 2008年 / 30卷 / 05期
关键词：
SCC; pipeline fatigue; crack interaction;
D O I：
10.1016/j.ijfatigue.2007.06.006
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
A section of gas pipeline containing stress corrosion cracking (SCC) was removed from service and pressure cycled. SCC cracks were shown to have extended by fatigue. Fatigue crack interaction was found to be a large factor in crack growth characteristics. Crack interaction was found to be influenced by original SCC crack inclination and layout. Fatigue crack growth was found to be independent of original SCC crack profile or aspect ratio. (C) 2007 Elsevier Ltd. All rights reserved.
引用
收藏
页码：850 / 860
页数：11
相关论文
共 50 条
  • [31] Experimental Studies on the Full-scale Fatigue Performance of X65 Marine Pipeline
    Hu, Yan-Hua
    Tang, De-Yu
    Fang, Zong-Tao
    Niu, Hu-Li
    INNOVATIVE MATERIALS: ENGINEERING AND APPLICATIONS, 2014, 1052 : 555 - 560
  • [32] An evaluation of the resistance of pipeline steels to initiation and early growth of stress corrosion cracks
    Cerny, I
    Linhart, V
    ENGINEERING FRACTURE MECHANICS, 2004, 71 (4-6) : 913 - 921
  • [33] Repassivation behavior of X65 pipeline steel in fuel grade ethanol and its implications for the stress corrosion cracking mechanism
    Goodman, Lindsey R.
    Singh, Preet M.
    CORROSION SCIENCE, 2012, 65 : 238 - 248
  • [34] Evaluation of Tribological Behavior of X65, X70, and X80 Pipeline Steels in the Presence of Hydrogen
    Salehan, Reza
    Davani, Reza Khatib Zadeh
    Miresmaeili, Reza
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2024, 34 (4) : 2763 - 2774
  • [35] Characterization of corrosion of X65 pipeline steel under disbonded coating by scanning Kelvin probe
    Fu, A. Q.
    Cheng, Y. F.
    CORROSION SCIENCE, 2009, 51 (04) : 914 - 920
  • [36] Role of Sour Environments on the Corrosion Fatigue Growth Rate of X65 Pipe Steel
    Gui, F.
    Ramgopal, T.
    Muller, M. G.
    CORROSION, 2012, 68 (08) : 730 - 738
  • [37] Stress Corrosion Behavior of X65 Steel Welded Joint in Marine Environment
    Wan, Hongxia
    Liu, Zhiyong
    Du, Cuiwei
    Song, Dongdong
    Li, Xiaogang
    INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE, 2015, 10 (10): : 8437 - 8446
  • [38] Synergistic effect of stray current and stress on corrosion of API X65 steel
    Wang, Xinhua
    Tang, Xinghua
    Wang, Liwei
    Wang, Cui
    Zhou, Wenqing
    JOURNAL OF NATURAL GAS SCIENCE AND ENGINEERING, 2014, 21 : 474 - 480
  • [39] Welding heat input for synergistic improvement in toughness and stress corrosion resistance of X65 pipeline steel with pre-strain
    Han, Yongdian
    Zhong, Shifang
    Tian, Lei
    Fei, Jiyuan
    Sun, Youhui
    Zhao, Lei
    Xu, Lianyong
    CORROSION SCIENCE, 2022, 206
  • [40] Effect of Temperature on Corrosion and Cathodic Protection of X65 Pipeline Steel in 3.5% NaCl Solution
    Liu, Yingjie
    Gao, Zhiming
    Lu, Xibo
    Wang, Liqin
    INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE, 2019, 14 (01): : 150 - 160
12345