Fatigue of stress corrosion cracks in X65 pipeline steels

被引：31
|
作者：
Gamboa, E. [1 ]
Linton, V. [1 ]
Law, M. [2 ]
机构：
[1] Univ Adelaide, Sch Mech Engn, Adelaide, SA 5005, Australia
[2] Australian Nucl Sci & Technol Org, PMBI, Menai, NSW 2234, Australia
来源：
INTERNATIONAL JOURNAL OF FATIGUE | 2008年 / 30卷 / 05期
关键词：
SCC; pipeline fatigue; crack interaction;
D O I：
10.1016/j.ijfatigue.2007.06.006
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
A section of gas pipeline containing stress corrosion cracking (SCC) was removed from service and pressure cycled. SCC cracks were shown to have extended by fatigue. Fatigue crack interaction was found to be a large factor in crack growth characteristics. Crack interaction was found to be influenced by original SCC crack inclination and layout. Fatigue crack growth was found to be independent of original SCC crack profile or aspect ratio. (C) 2007 Elsevier Ltd. All rights reserved.
引用
收藏
页码：850 / 860
页数：11
相关论文
共 50 条
  • [1] Corrosion fatigue behavior of X65 pipeline steel welded joints under different stress ranges
    Liu X.
    Zhong S.
    Xu L.
    Zhao L.
    Han Y.
    Hanjie Xuebao/Transactions of the China Welding Institution, 2023, 44 (07): : 24 - 31+78
  • [2] STRESS CORROSION CRACKING BEHAVIOR AND MECHANISM OF X65 AND X80 PIPELINE STEELS IN HIGH pH SOLUTION
    Zhu Min
    Liu Zhiyong
    Du Cuiwei
    Li Xiaogang
    Li Jiankuan
    Li Qiong
    Jia Jinghuan
    ACTA METALLURGICA SINICA, 2013, 49 (12) : 1590 - 1596
  • [3] High-pH inclined stress corrosion cracking in Australian and Canadian gas pipeline X65 steels
    Lavigne, O.
    Gamboa, E.
    Griggs, J.
    Luzin, V.
    Law, M.
    Roccisano, A.
    MATERIALS SCIENCE AND TECHNOLOGY, 2016, 32 (07) : 684 - 690
  • [4] Microstructure of X52 and X65 pipeline steels
    Wang, JQ
    Atrens, A
    Cousens, DR
    Kinaev, N
    JOURNAL OF MATERIALS SCIENCE, 1999, 34 (08) : 1721 - 1728
  • [5] Microstructure of X52 and X65 pipeline steels
    J. Q. Wang
    A. Atrens
    D. R. Cousens
    N. Kinaev
    Journal of Materials Science, 1999, 34 : 1721 - 1728
  • [6] A comparison of hydrogen permeation and the resulting corrosion enhancement of X65 and X80 pipeline steels
    Peng, X. Y.
    Cheng, Y. F.
    CANADIAN METALLURGICAL QUARTERLY, 2014, 53 (01) : 107 - 111
  • [7] Effects of microstructure banding on hydrogen assisted fatigue crack growth in X65 pipeline steels
    Ronevich, Joseph A.
    Somerday, Brian P.
    San Marchi, Chris W.
    INTERNATIONAL JOURNAL OF FATIGUE, 2016, 82 : 497 - 504
  • [8] Effect of Pseudomonas aeruginosa on corrosion of X65 pipeline steel
    Tang, Jianhua
    Guo, Ruiqi
    Zhang, Xin
    Zhao, Xu
    HELIYON, 2022, 8 (12)
  • [9] Corrosion behavior of X65 pipeline steel in coastal areas
    Sun, BaoZhuang
    Liao, Wenju
    Li, Zhong
    Liu, Zhiyong
    Du, Cuiwei
    ANTI-CORROSION METHODS AND MATERIALS, 2019, 66 (03) : 286 - 293
  • [10] Microbial corrosion behavior of x65 pipeline steel in product pipeline sediments
    Wang, Zheng-Quan
    Xu, Wei-Chen
    Zhou, Zi-Yang
    Yang, Li-Hui
    Li, Yan-Tao
    Surface Technology, 2020, 49 (07): : 245 - 254
12345