EFFECT OF MOLYBDATE ON THE STRESS CORROSION CRACKING OF 2205 DUPLEX STAINLESS STEEL IN SULFURIC ACID SOLUTION

被引：1
作者：
Yi, Guo [1 ]
Xing, Shanshan [1 ]
Qi, Haoyu [1 ]
Xu, Junhua [1 ]
Zheng, Chuanbo [1 ]
机构：
[1] Jiangsu Univ Sci & Technol, Sch Mat Sci & Engn, Zhenjiang 212003, Jiangsu, Peoples R China
来源：
MATERIALI IN TEHNOLOGIJE | 2019年 / 53卷 / 06期
关键词：
duplex stainless steel; electrochemical impedance spectroscopy; hydrogen permeation; molybdate; stress corrosion cracking; HYDROGEN PERMEATION BEHAVIOR; PITTING CORROSION; CARBON-STEEL; INHIBITION; TEMPERATURE; 304-STAINLESS-STEEL; PH;
D O I：
10.17222/mit.2018.124
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The inhibition effect of molybdate on stress corrosion cracking (SCC) was investigated by many researchers, but few considered the molybdate effect on hydrogen permeation and the relationship between SCC and hydrogen permeation. This paper presents the effect of molybdate on SCC susceptibility and hydrogen permeation through the 2205 super duplex stainless steel in a sulfuric acid solution. An addition of molybdate has an interesting influence. It decreases the SCC susceptibility. With its increasing concentration, the inhibition effect on the hydrogen permeation remains steady. Attempts were made to understand this behaviour based on the role of molybdate in hydrogen permeation and pitting characteristics of the 2205 stainless steel in a sulfuric acid solution.
引用
收藏
页码：797 / 804
页数：8
相关论文
共 50 条
[21]   Corrosion behavior of 2205 duplex stainless steel in NaCl solutions containing sulfide ions [J].
Xiao, Ying ;
Tang, Junlei ;
Wang, Yingying ;
Lin, Bing ;
Nie, Zhen ;
Li, Yunfei ;
Normand, Bernard ;
Wang, Hu .
CORROSION SCIENCE, 2022, 200
[22]   Electrochemical and Corrosion Behavior of 2205 Duplex Stainless Steel in Simulated Concrete Pore Solution [J].
Li, Baosong ;
Zhang, Weiwei .
INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE, 2017, 12 (09) :8432-8446
[23]   Effect of Temperature on Resistance to Pitting Corrosion in Duplex Stainless Steel 2205 Welds [J].
Martinez-Galvan, Y. ;
Dzib-Perez, L. ;
Garcia-Renteria, M. ;
Bilyy, O. ;
Lopez-Morelos, V. ;
Gonzalez-Sanchez, J. .
MATERIALS SCIENCE, 2023, 58 (06) :755-761
[24]   Effect of Temperature on Resistance to Pitting Corrosion in Duplex Stainless Steel 2205 Welds [J].
Y. Martinez-Galvan ;
L. Dzib-Perez ;
M. Garcia-Renteria ;
O. Bilyy ;
V. Lopez-Morelos ;
J. Gonzalez-Sanchez .
Materials Science, 2023, 58 (6) :755-761
[25]   Effect of microstructure on mechanical properties and corrosion resistance of 2205 duplex stainless steel [J].
Labanowski, Jerzy ;
Swierczynska, Aleksandra ;
Topolska, Santina .
POLISH MARITIME RESEARCH, 2014, 21 (04) :108-112
[26]   Role of nitrite addition in chloride stress corrosion cracking of a super duplex stainless steel [J].
Raman, R. K. Singh ;
Siew, W. H. .
CORROSION SCIENCE, 2010, 52 (01) :113-117
[27]   Atmospheric-Induced Stress Corrosion Cracking of Grade 2205 Duplex Stainless Steel-Effects of 475 °C Embrittlement and Process Orientation [J].
Ornek, Cem ;
Idris, Safwan A. M. ;
Reccagni, Pierfranco ;
Engelberg, Dirk L. .
METALS, 2016, 6 (07)
[28]   Stress Corrosion Cracking Behavior of Duplex Stainless Steel by Slow Strain Rate Tests [J].
Sanchez, J. ;
Fullea, J. ;
Andrade, C. ;
Alonso, C. .
CORROSION, 2009, 65 (02) :154-159
[29]   Characteristics of Cracking Propagation During Sulfide Stress Corrosion of Hot-Rolled Duplex Stainless Steel 2205 [J].
Gonzaga, A. C. ;
Barros, T. S. ;
Breves, I. M. S. ;
Pimenta, A. R. ;
Tavares, S. S. M. .
JOURNAL OF FAILURE ANALYSIS AND PREVENTION, 2024, 24 (01) :309-317
[30]   Characteristics of Cracking Propagation During Sulfide Stress Corrosion of Hot-Rolled Duplex Stainless Steel 2205 [J].
A. C. Gonzaga ;
T. S. Barros ;
I. M. S. Breves ;
A. R. Pimenta ;
S. S. M. Tavares .
Journal of Failure Analysis and Prevention, 2024, 24 :309-317
12345