Role of thickness on electrochemical behaviour of Ni2Si coatings in NaCl solution

被引：2

作者：

Verdian, M. M. ^{[1
]}

Raeissi, K. ^{[2
]}

Salehi, M. ^{[2
]}

机构：

[1] Islamic Azad Univ, Dept Mat Engn, Najafabad Branch, Najafabad, Isfahan, Iran

[2] Isfahan Univ Technol, Dept Mat Engn, Esfahan 8415683111, Iran

来源：

TRANSACTIONS OF THE INSTITUTE OF METAL FINISHING | 2015年 / 93卷 / 03期

关键词：

Intermetallic; Ni2Si; Coating; HVOF; Corrosion; NaCl; CORROSION-RESISTANCE; INTERMETALLIC COATINGS;

D O I：

10.1179/0020296715Z.000000000241

中图分类号：

O646 [电化学、电解、磁化学];

学科分类号：

081704 ;

摘要：

Ni2Si intermetallic coatings were deposited on a substrate of 420 stainless steel using a high velocity oxy-fuel (HVOF) process. The electrochemical corrosion behaviour of the coatings in 3.5% NaCl solution was investigated by means of Tafel polarisation tests and electrochemical impedance spectroscopy (EIS) measurements. Two coatings with different thicknesses, 55 and 115 mm, were investigated. The results showed that the corrosion rate of the thicker coating was lower than that of stainless steel by one order of magnitude. Local attack of the substrate was observed after the polarisation test of this coating, while the coating was still intact. The thinner coating and the stainless steel substrate showed similar corrosion rates. In this case, the substrate was severely attacked after the polarisation test. Two time constants were observed in the EIS spectra of both coatings which were related to charge transfer processes and pore resistance, respectively.

引用

页码：164 / 168

页数：5

共 16 条

[1] Barsoukov E, 2005, IMPEDANCE SPECTROSCOPY: THEORY, EXPERIMENT, AND APPLICATIONS, 2ND EDITION, pXII
[2] Cramer Stephen D., 2004, CORROSION ENV IND C, V13C, P27
[3] Cramer Stephen D., 2004, CORROSION MAT B, V13B, P54
[4] Davis J. R., 2008, HDB THERMAL SPRAY TE
[5] Effects of thickness coating on the electrochemical behaviour of thermal spray Cr3C2-NiCr coatings
Guilemany, JM
Fernández, J
Delgado, J
Benedetti, AV
Climent, F
[J]. SURFACE & COATINGS TECHNOLOGY, 2002, 153 (2-3) : 107 - 113
[6] Electrochemical methods for characterisation of thermal spray corrosion resistant stainless steel coatings
Hofman, R
Vreijling, MPW
Ferrari, GM
de Wit, JHW
[J]. ELECTROCHEMICAL METHODS IN CORROSION RESEARCH VI, PTS 1 AND 2, 1998, 289-2 : 641 - 653
[7] Effect of Spray Parameters on the Corrosion Behavior of HVOF Sprayed WC-Co-Cr Coatings
Hong, Sheng
Wu, Yuping
Zheng, Yugui
Wang, Bo
Gao, Wenwen
Li, Gaiye
Ying, Guobing
Lin, Jinran
[J]. JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2014, 23 (04) : 1434 - 1439
[8] Microstructure and electrochemical properties of nanostructured WC-10Co-4Cr coating prepared by HVOF spraying
Hong, Sheng
Wu, Yuping
Zheng, Yugui
Wang, Bo
Gao, Wenwen
Lin, Jinran
[J]. SURFACE & COATINGS TECHNOLOGY, 2013, 235 : 582 - 588
[9] Corrosion process in NaCl/Na2SO4 solutions of AISI 316L stainless steel treated by ionic nitriding
Santos, C. B.
Metzner, M.
Malfatti, C. F.
Ferreira, J. Zoppas
[J]. TRANSACTIONS OF THE INSTITUTE OF METAL FINISHING, 2009, 87 (06): : 309 - 314
[10] Corrosion resistance of Ni/Al2O3 coatings in NaCl solution
Szczygiel, B
Kolodziej, M
[J]. TRANSACTIONS OF THE INSTITUTE OF METAL FINISHING, 2005, 83 (04): : 181 - 187

← 1 2 →