X-Ray Diffraction Study, Magnetic Susceptibility, and Electric Properties of Cu3Fe0.5Se2 Crystal

被引：0
|
作者：
Guseinov, G. G. [1 ]
Ragimov, S. S. [1 ]
Barbaran, J. Hasani [1 ]
Agamirzoeva, G. M. [1 ]
机构：
[1] Natl Acad Sci, Inst Phys, AZ-1143 Baku, Azerbaijan
来源：
CRYSTALLOGRAPHY REPORTS | 2010年 / 55卷 / 04期
关键词：
Chalcopyrite; Barbaran; Crystallography Report; Azerbaijan; Antiferromagnetic State;
D O I：
10.1134/S1063774510040231
中图分类号：
O7 [晶体学];
学科分类号：
0702 ; 070205 ; 0703 ; 080501 ;
摘要：
Single crystals of the Cu3Fe0.5Se2 composition have been grown. The orthorhombic lattice parameters are found to be a = 8.169 angstrom, b = 8.238 angstrom, c = 12.052 angstrom, V = 811.15 angstrom(3), D-x = 6.23 g/cm(3), sp. gr. Pnma, Z = 8. The magnetic susceptibility is measured in the range 100 < T < 400 K at H = 2 T. It is established that a crystal transforms into the antiferromagnetic state below T-N = 350 K. The temperature dependences of the electrical conduction (sigma), thermal electromotive force (alpha), and thermal conduction (k) are measured in the range 80 < T < 400 K; the n value was calculated to be 5 x 10(19) cm(-1).
引用
收藏
页码：673 / 675
页数：3
相关论文
共 48 条
  • [1] X-ray diffraction study, magnetic susceptibility, and electric properties of Cu3Fe0.5Se2 crystal
    G. G. Guseinov
    S. S. Ragimov
    J. Hasani Barbaran
    G. M. Agamirzoeva
    Crystallography Reports, 2010, 55 : 673 - 675
  • [2] Growth and X-ray diffraction study of Rb2Na(NO3)3 crystals
    V. I. Nasirov
    N. M. Namazova
    G. G. Guseinov
    A. S. Amirov
    Crystallography Reports, 2015, 60 : 841 - 843
  • [3] X-ray diffraction study of (TlInSe2)1−x(TlGaTe2)x crystal system
    A. U. Sheleg
    E. M. Zub
    A. Ya. Yachkovskii
    S. N. Mustafaeva
    E. M. Kerimova
    Crystallography Reports, 2012, 57 : 283 - 285
  • [4] X-ray diffraction study of compounds in the Ag2S-Cu2S system
    Yu. G. Asadov
    Yu. I. Alyev
    K. M. Jafarov
    Inorganic Materials, 2008, 44
  • [5] X-ray diffraction study of compounds in the Ag2S-Cu2S system
    Asadov, Yu. G.
    Alyev, Yu. I.
    Jafarov, K. M.
    INORGANIC MATERIALS, 2008, 44 (05) : 460 - 466
  • [6] X-ray diffraction study of the crystallographic characteristics of TlInSxSe2 − x solid solutions
    A. U. Sheleg
    V. G. Hurtavy
    V. V. Shautsova
    V. A. Aliev
    Crystallography Reports, 2014, 59 : 186 - 189
  • [7] Synthesis and X-ray diffraction study of Cu2ZnSn(SxSe1-x)4 solid solutions
    A. U. Sheleg
    V. G. Hurtavy
    V. A. Chumak
    Crystallography Reports, 2015, 60 : 758 - 762
  • [8] Phase transitions and transport properties of Cu3Co0.5Se2 crystals
    J. Hasani Barbaran
    G. G. Guseinov
    V. A. Gasymov
    S. S. Ragimov
    Inorganic Materials, 2012, 48 : 786 - 788
  • [9] Determination of the magnetic contribution to the YFe2 susceptibility by means of X-ray resonant magnetic reflectivity
    A. Smekhova
    M. A. Andreeva
    E. E. Odintsova
    C. Dufour
    K. Dumesnil
    F. Wilhelm
    A. Rogalev
    Crystallography Reports, 2010, 55 : 854 - 862
  • [10] Synthesis and X-ray diffraction study of (Cs0.5Ba0.25)[UO2(CH3COO)3] and Ba0.5[UO2(CH3COO)3]
    L. B. Serezhkina
    A. V. Vologzhanina
    V. V. Klepov
    V. N. Serezhkin
    Crystallography Reports, 2011, 56 : 265 - 269
12345