Formation of NO and SO2 in the Sintering Process of Iron Ores

Nitric oxide (NO) and sulfur dioxide (SO2) are the major environmental pollutants being generated in the steel industry. More than half of NO and SO2 are emitted from sinter plants. Due to the catalytic effect of CaO in the sinter mix on the formation of NO and SO2, it might differ from that in the combustion of raw coals. In the combustion of raw coals, both NO and SO2 were formed in the temperature range of 473 K (200 degrees C) to 1623 K (1350 degrees C). In the case where the content of endogenous CaO in coal ash was high, the formation of SO2 was significantly reduced below 1473 K (1200 degrees C). In the case of the sinter mix, NO was formed in the temperature range of 473 K (200 degrees C) to 1173 K (900 degrees C) and the conversion of N to NO was increased by the catalytic effect of CaO in the sinter mix. Most of the SO2 was formed above 1473 K (1200 degrees C). The CaO present in the sinter mix reacted with the SO2 generated below 1473 K (1200 degrees C) to form CaSO4, the stability of which was maintained until 1473 K (1200 degrees C); thus, the conversion of S to SO2 was reduced. Based on the coal composition and functionalities of nitrogen and sulfur in coals, the indices of NO and SO2 were proposed to predict the conversion of N to NO and S to SO2, respectively. The increased heating rate shifted the formation temperature range of NO to higher temperatures and increased the formation of SO2 by the thermally activated decomposition of CaSO4.