Effect of oxygen boost diffusion treatment on fatigue behavior of Ti-4Al-2V alloy

被引：17
|
作者：
Omidbakhsh, F. [1 ]
Ebrahimi, A. R. [1 ]
Mousavi, S. H. [1 ]
Khosroshahi, R. A. [1 ]
Nazarpour, S. [2 ]
机构：
[1] Sahand Univ Technol, Dept Mat Engn, Tabriz, Iran
[2] Univ Barcelona, Dept Elect, Barcelona 08028, Spain
来源：
SURFACE & COATINGS TECHNOLOGY | 2011年 / 205卷 / 8-9期
关键词：
Oxygen boost diffusion; Residual compressive stress; Fatigue crack closure; Ti-4Al-2V; DLC COATINGS; TITANIUM; OXIDATION; PROPAGATION; RESISTANCE; MORPHOLOGY; TI6AL4V; STRESS;
D O I：
10.1016/j.surfcoat.2010.11.004
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
An attempt has been made to determine the influence of oxygen boost diffusion (OBD) treatment on the fatigue behavior of Ti-4Al-2V alloy. In order to study the effect of OBD treatment, specimens were thermally oxidized at 450 degrees C in air for 2 h. Pre oxidized samples were put in the vacuum furnace (1 x 10(-3) Pa) at 850 degrees C for 7, 14, and 21 h. Rotary bending fatigue tests were performed on specimens before and after OBD treatments. The results revealed that OBD treatment led the fatigue endurance limit to be increased up to 85%. X-ray diffraction studies revealed that OBD treatment gave rise to large lattice expansion and high amount of residual compressive stresses, as result of dissolving oxygen atoms as interstitial in the titanium lattice. It is believed that the fatigue endurance limit improvement is mainly due to the residual compressive stress (RCS) filed and fatigue crack closure mechanisms. (C) 2010 Elsevier B.V. All rights reserved.
引用
收藏
页码：2954 / 2963
页数：10
相关论文
共 50 条
  • [21] The Effect of Plasma Nitriding on the Fatigue Behavior of the Ti-6Al-4V Alloy
    de Castro, Michele C. B.
    Couto, Antonio A.
    Almeida, Gisele F. C.
    Massi, Marcos
    de Lima, Nelson B.
    da Silva Sobrinho, Argemiro
    Castagnet, Mariano
    Xavier, Gleicy L.
    Oliveira, Rene R.
    MATERIALS, 2019, 12 (03)
  • [22] The mechanical property and microstructure of Ti-4Al-2V alloy after high speed shot peening treatment
    Zhang, Xiyan
    Jia, Chong
    Zhao, Xinchun
    Liu, Zhinong
    Yi, Jin
    PROGRESSES IN FRACTURE AND STRENGTH OF MATERIALS AND STRUCTURES, 1-4, 2007, 353-358 : 730 - +
  • [23] Influence of Oxygen Diffusion Treatment on Seizure Resistance of Ti6Al4V Alloy
    Takahashi, Kyo
    Sato, Eiichi
    JOURNAL OF THE JAPAN INSTITUTE OF METALS, 2008, 72 (12) : 997 - 1001
  • [24] Study of δ-hydrides in Ti-2Al-2.5Zr and Ti-4Al-2V alloys
    Yu, H
    Gu, JL
    Liu, Q
    Liu, YZ
    RARE METALS, 2006, 25 (01) : 16 - 20
  • [25] Effect of hydrogen on diffusion bonding behavior and mechanism of Ti-6Al-4V alloy
    Li, Zhiqiang
    Han, Kun
    Hou, Hongliang
    Wang, Baoyu
    Hu, Zhenghuan
    Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering, 2014, 43 (02): : 306 - 310
  • [26] Effect of Hydrogen on Diffusion Bonding Behavior and Mechanism of Ti-6Al-4V alloy
    Li Zhiqiang
    Han Kun
    Hou Hongliang
    Wang Baoyu
    Hu Zhenhuan
    RARE METAL MATERIALS AND ENGINEERING, 2014, 43 (02) : 306 - 310
  • [27] Study of δ-hydrides in Ti-2Al-2.5Zr and Ti-4Al-2V alloys
    YU Huang
    RareMetals, 2006, (01) : 16 - 20
  • [28] Irradiation behavior of Ti-4Al-2V (IIT-3B) alloy for ITER blanket modules flexible attachment
    Rodchenkov, B. S.
    Kozlov, A. V.
    Kuznetsov, Yu. G.
    Kalinin, G. M.
    Strebkov, Yu. S.
    JOURNAL OF NUCLEAR MATERIALS, 2007, 367 : 1312 - 1315
  • [29] Fatigue small crack behavior of Ti-6Al-4V alloy
    Hu, Ben-Run
    Wu, Xue-Ren
    Ding, Chuan-Fu
    Hangkong Cailiao Xuebao/Journal of Aeronautical Materials, 2000, 20 (03): : 36 - 37
  • [30] Fatigue behavior of PVD coated Ti-6Al-4V alloy
    Costa, M. Y. P.
    Venditti, M. L. R.
    Cioffi, M. O. H.
    Voorwald, H. J. C.
    Guimaraes, V. A.
    Ruas, R.
    INTERNATIONAL JOURNAL OF FATIGUE, 2011, 33 (06) : 759 - 765
12345