Preparation of diamond/aluminum composite with titanium coating on diamond powder by microwave technology

In this research, the diamond particles were coated with titanium by microwave heating method, then the Ti-coated diamond particles were used as raw material to fabricate the diamond/Al composites by microwave sintering. The result shows that the diamond particles could be covered with a uniform and continuous Ti coating under microwave irradiation, and the best Ti coating was obtained at 810 degrees C for 1 h. The metallic bond between diamond and Ti was formed to generate the intermediate transition layer of TiC. The diamond/Al composites which used Ti-coated diamond particles as raw material and were fabricated by microwave sintering show high relative density and hardness. The relative density and hardness of the diamond/Al composites increased with the temperature. While the composites were sintered at 710 degrees C for 1 h, the density could reach 2.855 g.cm(-3), and relative density was 92.09%, which shows better microstructures and properties. There is Al3Ti alloy phase in Ti-coated diamond/Al composites, so the Ti-coated diamond can be well combined with the Al matrix, which can further improve the properties of the composites.