Influence of Mn-Ni alloying elements on surface film and pitting resistance of Cr-Mn austenitic stainless steels

被引：14
作者：
Qu, H. P. [1 ]
Chen, H. T. [1 ]
Lang, Y. P. [1 ]
机构：
[1] CISRI, Inst Special Steels, 76 Haidiannan Rd, Beijing, Peoples R China
来源：
CONSTRUCTION AND BUILDING MATERIALS | 2016年 / 125卷
关键词：
Stainless steel; XPS; Argon sputter; Passive film; Pitting potential; PASSIVE FILM; CORROSION BEHAVIOR; HIGH-TEMPERATURE; XPS; CHLORIDE; AES; INCLUSIONS; MANGANESE;
D O I：
10.1016/j.conbuildmat.2016.08.059
中图分类号：
TU [建筑科学];
学科分类号：
0813 ;
摘要：
This research focused on surface film and corrosion resistance of three commercial type 200 austenitic stainless steels including L4, L1 and LH with different Mn/Ni mass ratio in Chinese market. X-ray photoelectron spectrum (XPS) results showed that Fe, Cr and Mn oxide layer thickness and passive film thickness were reduced as Mn/Ni mass ratio increased. Mn enrichment was only found in LH passive film. Mn oxide percentage in LH passive film was also the highest. These disadvantages deteriorated pitting resistance of LH, which was proved by anodic polarization result. Mn/Ni mass ratio should not be higher than 1.7 to ensure good corrosion resistance and low raw material cost. (C) 2016 Elsevier Ltd. All rights reserved.
引用
收藏
页码：427 / 437
页数：11
相关论文
共 23 条
[1]   ELECTROCHEMICAL AND XPS STUDIES OF THE EFFECTS OF GAMMA-RAY IRRADIATION ON THE PASSIVE FILM ON 446-STAINLESS STEEL [J].
CAPOBIANCO, G ;
PALMA, G ;
GRANOZZI, G ;
GLISENTI, A .
CORROSION SCIENCE, 1992, 33 (05) :729-734
[2]   XPS analysis of manganese in stainless steel passive films on 1.4432 and the lean duplex 1.4162 [J].
Fredriksson, W. ;
Edstrom, K. ;
Olsson, C. -O. A. .
CORROSION SCIENCE, 2010, 52 (07) :2505-2510
[3]   XPS depth profiling study on the passive oxide film of carbon steel in saturated calcium hydroxide solution and the effect of chloride on the film properties [J].
Ghods, P. ;
Isgor, O. B. ;
Brown, J. R. ;
Bensebaa, F. ;
Kingston, D. .
APPLIED SURFACE SCIENCE, 2011, 257 (10) :4669-4677
[4]   Effect of chromium content and sweep rate on passive film growth on iron-chromium alloys studied by EQCM and XPS [J].
Hamm, D ;
Olsson, COA ;
Landolt, D .
CORROSION SCIENCE, 2002, 44 (05) :1009-1025
[5]   Electrochemical properties and growth mechanism of passive films on Alloy 690 in high-temperature alkaline environments [J].
Huang, Junbo ;
Wu, Xinqiang ;
Han, En-Hou .
CORROSION SCIENCE, 2010, 52 (10) :3444-3452
[6]   XPS characterization of passive films formed on Type 304 stainless steel in humid atmosphere [J].
Jung, Rock-Hoon ;
Tsuchiya, Hiroaki ;
Fujimoto, Shinji .
CORROSION SCIENCE, 2012, 58 :62-68
[7]   THE PASSIVITY OF IRON-CHROMIUM ALLOYS [J].
KIRCHHEIM, R ;
HEINE, B ;
FISCHMEISTER, H ;
HOFMANN, S ;
KNOTE, H ;
STOLZ, U .
CORROSION SCIENCE, 1989, 29 (07) :899-917
[8]   Electrochemical and XPS studies of the passive film formed on stainless steels in borate buffer and chloride solutions [J].
Kocijan, Aleksandra ;
Donik, Crtomir ;
Jenko, Morlika .
CORROSION SCIENCE, 2007, 49 (05) :2083-2098
[9]  
Krawiec H., 2006, PASS MET SEM PROP TH, P567
[10]   A study on the initiation of pitting corrosion in carbon steel in chloride-containing media using scanning electrochemical probes [J].
Lin, Bin ;
Hu, Ronggang ;
Ye, Chenqing ;
Li, Yan ;
Lin, Changjian .
ELECTROCHIMICA ACTA, 2010, 55 (22) :6542-6545
123