A study on the preparation, dielectric properties and electrical conductivity of glass fiber bulk yarn fabrics with a graphite coating

被引:1
作者
Liu, Yuanjun [1 ]
Sun, Tian [1 ]
Zhao, Xiaoming [1 ]
机构
[1] Tianjin Polytech Univ, Sch Text, 399 Binshui West Rd, Tianjin 300387, Peoples R China
关键词
Graphite; coating; glass fiber bulk yarn fabrics; dielectric constant; electrical conductivity; MICROWAVE ABSORBING PROPERTIES; COMPOSITES; IRON;
D O I
10.1080/00405000.2020.1743479
中图分类号
TB3 [工程材料学]; TS1 [纺织工业、染整工业];
学科分类号
0805 ; 080502 ; 0821 ;
摘要
A glass fiber bulk yarn fabric with a graphite coating was produced, with the glass fiber bulk yarn fabric used as the base material, E44 epoxy resin as adhesive, low molecular 650 polyamide as curing agent and graphite, due to its low cost and low density, as the absorbing material. The influences of the graphite content, coating thickness and drying temperature on the dielectric constant and conductivity were the main focus of the investigation. The results showed that the glass fiber bulk yarn fabrics prepared with the graphite coating have good dielectric properties. In the frequency range used in the study, the content, drying temperature and coating thickness for the graphite coating were found to have a major influence on the real and imaginary parts of the dielectric constant, loss tangent value and the real and imaginary parts of the electrical conductivity.
引用
收藏
页码:8 / 15
页数:8
相关论文
共 22 条
[1]   Electromagnetic and Electrical Properties of Coated Cotton Fabric with Barium Ferrite Doped Polyaniline Film [J].
Aksit, Aysun Cireli ;
Onar, Nurhan ;
Ebeoglugil, M. Faruk ;
Birlik, Isil ;
Celik, Erdal ;
Ozdemir, Ismail .
JOURNAL OF APPLIED POLYMER SCIENCE, 2009, 113 (01) :358-366
[2]   Absorbing properties and structural design of microwave absorbers based on carbonyl iron and barium ferrite [J].
Feng, Y. B. ;
Qiu, T. ;
Shen, C. Y. .
JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 2007, 318 (1-2) :8-13
[3]  
Folgueras Luiza de Castro, 2007, Mat. Res., V10, P95
[4]   Role of functional groups on the microwave attenuation and electric resistivity of activated carbon fiber cloth [J].
Hashisho, Zaher ;
Rood, Mark J. ;
Barot, Suhail ;
Bernhard, Jennifer .
CARBON, 2009, 47 (07) :1814-1823
[5]   Microwave absorbing properties of NiZn-ferrite synthesized from waste iron oxide catalyst [J].
Hwang, Yeon .
MATERIALS LETTERS, 2006, 60 (27) :3277-3280
[6]   MICROWAVE ABSORBING PROPERTIES OF SINTERED NI-ZN FERRITE [J].
KIM, SS ;
HAN, DH ;
CHO, SB .
IEEE TRANSACTIONS ON MAGNETICS, 1994, 30 (06) :4554-4556
[7]   The use of carbon/dielectric fiber woven fabrics as filters for electromagnetic radiation [J].
Lee, Sang-Eui ;
Park, Ki-Yeon ;
Oh, Kyoung-Sub ;
Kim, Chun-Gon .
CARBON, 2009, 47 (08) :1896-1904
[8]   Absorption properties of carbon black/silicon carbide microwave absorbers [J].
Liu, Xiangxuan ;
Zhang, Zeyang ;
Wu, Youpeng .
COMPOSITES PART B-ENGINEERING, 2011, 42 (02) :326-329
[9]   The research of EM wave absorbing properties of ferrite/silicon carbide double coated polyester woven fabric [J].
Liu, Yuanjun ;
Liu, Yuanchen ;
Zhao, Xiaoming .
JOURNAL OF THE TEXTILE INSTITUTE, 2018, 109 (01) :106-112
[10]   The influence of dopant type and dosage on the dielectric properties of polyaniline/nylon composites [J].
Liu, Yuanjun ;
Zhao, Xiaoming .
JOURNAL OF THE TEXTILE INSTITUTE, 2017, 108 (09) :1628-1633