Nitrogen-doped herringbone carbon nanofibers with large lattice spacings and abundant edges: Catalytic growth and their applications in lithium ion batteries and oxygen reduction reactions

N-doped herringbone carbon nanofibers (N-HBCNFs) were efficiently fabricated by chemical vapor deposition on Ni nanoparticles derived from layered double hydroxide precursors. The as-obtained CNFs were with an average diameter of similar to 60 nm, a high purity of similar to 91.6%, and a large specific surface area of 108.1 m(2) g(-1). When employed as anode materials, the N-HBCNFs yielded a reversible capacity of 500.0 mAh g(-1) at a current density of 0.10 C (1.0 C = 372 mA g(-1)) and rapid lithium storage properties with a high capacity of 141.6 mAh g(-1) at 5.0 C. When the N-HBCNFs were used as catalyst for oxygen reduction reaction, an onset potential of 0.85 V, an electron transfer number of 3.1, and a current retention of 69.1% after 16,000 s test were detected, indicating the good reactivity of N-HBCNF catalyst for electrocatalysis application. The superior performance of N-HBCNFs was attributed to their enlarged graphitic lattice spacings and abundant edges on the surface, which afforded more active sites for both Li ion storage and oxygen reduction reaction. Thus, the N-HBCNFs are promising nanocarbon materials for various applications in lithium ion batteries, lithium-sulfur batteries, lithium-air batteries, fuel cells, and so on. (C) 2014 Elsevier B.V. All rights reserved.